Study On Debinding And Sintering Conditions In Extrusion-Based Additive Manufacturing Of 316l And 316l + Cu, Jean-François Silvain, Daniel Lincoln Gifford, Sébastien Fourcade, Laurent Cuzacq, Jean-Luc Grosseau-Poussard, Catherine Debiemme-Chouvy, Nicolas Tessier Doyen, Yongfeng Lu

Department of Electrical and Computer Engineering: Faculty Publications

This study investigates the use of a methylcellulose binder in extrusion additive manufacturing of 316L as an alternative to common wax-based binders. Various quantities of copper (Cu) powder were also added in the paste composition to attempt to reduce the sintering temperature by promoting persistent liquid phase sintering. Debinding experiments were conducted under different temperatures and dwell times using argon (Ar), Ar/5%H₂, and Ar/1%O₂ atmospheres. Debinding reduced carbon (C) content to 0.032 wt.% by using a two-step debinding process of Ar/5%H₂ and Ar/1%O₂ thermal treatments. Using this debinding process, sintering was conducted at 1200 ^{o …}