Characterization Of Aluminum-Boron Carbide Particulate Metal Matrix Composites, Eric Blank

Materials Engineering

The analysis of die-cast 380 aluminum-boron carbide particulate metal matrix composites (MMC) was performed in order to see if the samples had the required tensile strength of 300 MPa. 10wt% B4C die-cast samples were produced and tested. Half were heat treated to the T6 condition and the others were left as cast. Using ASTM standard B 557M it was found that the average tensile strength for the as-cast samples was 130 MPa and the heat treated samples had a tensile strength of 93 MPa. These values were both lower than expected. The heat treated samples were not expected to have …