Erosion Resistance Of Tungsten-Carbide Coatings For Steel Pipes In Fluid Catalytic Cracking Units, Davis Vannasing, Jennifer Hulfachor
Erosion Resistance Of Tungsten-Carbide Coatings For Steel Pipes In Fluid Catalytic Cracking Units, Davis Vannasing, Jennifer Hulfachor
Materials Engineering
In petroleum processing, the flow of catalyst readily leads to erosion of piping in a fluid catalytic cracking unit. Advances in coating materials and processes necessitate a re-evaluation of current protection methods. Commercially available tungsten-carbide (WC) claddings and nanostructured WC-W CVD coatings were investigated as potential alternative erosion-resistant coatings. Erosion tests by solid particle impingement were conducted on 2 variations of claddings and 1 variation of WC-W coatings following ASTM standard G76. A36 steel coupons were used as reference samples. For statistical validation, 2-3 replications of the tests were performed for the claddings and WC-W coating. Testing was conducted using …
Investigation Of Copper Infiltration Alloys For Use In Metal Matrix Composite Drill Bits, Samuel J. Stueland, Timothy P. Markiewicz
Investigation Of Copper Infiltration Alloys For Use In Metal Matrix Composite Drill Bits, Samuel J. Stueland, Timothy P. Markiewicz
Materials Engineering
A newly developed copper-based alloy, P98-X1 was tested for compressive strength to predict qualitative performance compared to MF53, F-Bronze, CuNiSn, and CuMnNi for use as the infiltration alloy in metal matrix composite (MMC) drill bits. Ingots of each alloy were cast using an arc furnace and cut into compression testing samples using wire electrical discharge machining (EDM). The alloys were selected for testing based on solid solution strengthening coefficient and melting point. Five of each alloy were compression tested to determine yield strength of the infiltration alloy. Yield strength was determined using a 0.002mm displacement offset from the linear elastic …