Compressive Creep Of Basic Refractories, Maurice E. Green
Compressive Creep Of Basic Refractories, Maurice E. Green
Masters Theses
"The microstructure and mineralogical composition of direct bonded, 50 wt.% magnesia - 50 wt.% chrome ore refractory compositions containing controlled additions of silica were correlated with their compressive creep behavior in the temperature range 1450⁰ to 1550⁰C under stresses of 100 to 175 psi. Steady state creep rates were determined from the linear regression of the steady state regions of deformation on time. Apparent activation energies and deformation flow characteristics were determined from the temperature and stress dependence of the steady state creep rates. Silica contents up to 3.5 wt.% increased the amount of direct intergranular bonding which decreased the …
Kinetics Of The Formation Of Strontium Zirconate, W. H. Parker
Kinetics Of The Formation Of Strontium Zirconate, W. H. Parker
Masters Theses
"The decomposition rate of strontium carbonate (SrC0₃) was measured using a TGA apparatus. It was found to deviate slightly from zero order classical reaction. The rate of formation of strontium zirconate (SrZr0₃) from zirconium oxide (ZrO₂) and strontium oxide (SrO) in the form of the decomposition product of SrCO₃ was measured using quantitative x-ray diffraction for mineralogical analysis. It was found to most nearly follow the Zhuravlev-Lesokhin-Tempel' man rate equation. The rate of decomposition of strontium carbonate was found to be more rapid than the rate of formation of strontium zirconate such that for the most part strontium oxide is …