Engineering Commons^™

A Rubric For Electrochemical Testing Of Metallic Biomaterials, Frederick G. De La Fuente

Master's Theses

Corrosion is a major factor for the failure of metallic medical implants. Testing a metal’s suseptability to corrosion prior to implantation is key to a successful implantation. Electrochemical processes were used in this study to evaluate the characteristics of corrosion of both AISI 316 stainless steel and titanium alloy Ti6Al4V, welded and non-welded. Linear, potentiodynamic, and cyclic polarization curves were produced by the PARC 2273 potentiostat showing the corrosion tendencies of the metals in four unique solutions 3.5% NaCl, 0.35% NaCl, phosphate buffered saline solution (PBS), and Butterfield phosphate buffered solution (BPS). The concentration of chloride ions in solutions affected …

Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner

Materials Engineering

To assess corrosion rates of metal alloy bio-absorbable stents an experimental set-up was designed to mimic the coronary artery environment. The artery was modeled using 4mm diameter Tecoflex tubing and the metal alloy stents were inserted into the tubing using a catheter. As is the case in cardiac surgery, the catheter with the stent and a microballoon were maneuvered to the desired position. The microballoon was then slowly inflated to expand the stent and compress it against the tubing walls. The catheter and microballoon were then withdrawn. A circulating pump system was set up to cycle fetal bovine serum (FBS) …

Evaluation Of Corrosion Properties For Use Of Az31b In Bioabsorbable Stents And In Vivo Corrosion Rate Prediction Using Fea, Jared Vidales, Austin Schader, Jenna Jerman, Michael Turovskiy

Materials Engineering

AZ31B was heat treated to evoke more controlled and uniform corrosion. 1/16” diameter AZ31B wire was cut into six samples each 1” long. The samples underwent heat treatments following ASTM B661-06. Samples were weighed and placed into three different in vitro environments. In the first scenario two samples of each heat treatment were individually placed in 50 ml of saline solution at 0.9% sodium, in a static test tube at 37°C temperature. Two samples were placed in 100 ml of 0.9% saline solution in a 250 ml stirring beaker with an average whirlpool depth of 1”. Two of each sample …

Corrosion Of Stainless Steel 316l And Astm F75 Cobalt Chromium Alloy During Immersion Testing In Silver Salt Solutions, Meagan Higgins

Materials Engineering

This study evaluates the potential effects of silver salts on biocompatible metals used for prostheses during the chemical reduction process to produce a silver antimicrobial layer on the metal’s surface. Samples of two biocompatible metals were obtained: Stainless Steel 316L and ASTM F75 Cobalt Chromium Alloy. Three different silver salts were also acquired: silver nitrate, silver sulfadiazine, and silver chloride. Specimens of each metal were cut to size using a 4-1/2 inch aluminum oxide, 40 grit, cut off wheel for metal, attached to a Dewalt Angle Grinder. The biocompatible metal samples were then subject to either Solution 1, water with …

The Effect Of Particle Surface Area To Volume Ratio On Ion Release From Cocr Spheres, Darin J. Grandfield

Master's Theses

In 2005, over 200,000 Americans underwent a hip arthroplasty, the replacement of a hip joint with an artificial prosthesis. Of these arthroplasties, metal-on-metal type implants represent an increasing usage percentage. Metal-on-metal implants are selected largely for their low volumetric wear rate, durability, and resistance to corrosion. In spite of these advantages, little is known concerning the long-term consequences of heavy metal alloy use in the body, although early research indicates potentially carcinogenic results. This thesis is a preliminary investigation into these long term effects and their root causes.

An improved comprehension of the corrosion kinetics and the rate of ion …