Controlling Grain Size In Cold Worked And Annealed 1100 Aluminum To Optimize Ductility In Rocket Diaphragm Systems, Ryan Lewis, Bryce Simmons, Jessica Williams

Materials Engineering

Liquid propellant rocket diaphragms require extreme ductility. 1100 Aluminum is used for its high ductility, but the post-processing cold work and subsequent anneal result in excessively large grains. The effect of heat treatment and cold work on grain size in 1100 aluminum was explored. The samples were cold worked to 0, 5, 10, 15 and 30% using tensile elongation. The samples were then heat treated per AMS 2770 with either a "Steel Conduction" (1000 – 1150°F/min) or a "Production" (16 – 18°F/min) heating rate. The grain size of the samples were measured using the mean lineal intercept method. The grain …