Effect Of Time Delay Between Etching And Adhesive Bonding (“Outlife” Time) On Lap-Shear Strength Of Aluminum Alloys Using Environmentally-Friendly P2 Etch, Josh Barkhimer, Matthew Erich, Gokul Nair
Effect Of Time Delay Between Etching And Adhesive Bonding (“Outlife” Time) On Lap-Shear Strength Of Aluminum Alloys Using Environmentally-Friendly P2 Etch, Josh Barkhimer, Matthew Erich, Gokul Nair
Materials Engineering
Raytheon Company currently uses a Forest Products Laboratory (FPL) paste etchant for preparing aluminum surfaces for adhesive bonding, and FPL is a source of hazardous hexavalent chromium. The goal of this study was to evaluate a less-toxic P2 paste etchant as a possible replacement. Coupons of 2024-T3, 6061-T6, and 7075-T6 grades of aluminum alloy were solvent-degreased, abrasively cleaned, and etched at room temperature using P2 paste following a strict protocol adopted from Raytheon. Coupons were then left exposed to air for assigned time intervals (or “outlife” times) of 0, 1, 4, 8, 16, and 63 or 72 hours. The aluminum …
Characterization Of Laser Deposited Ti-6al-4v To Nb Gradient Alloys, Clincy Cheung
Characterization Of Laser Deposited Ti-6al-4v To Nb Gradient Alloys, Clincy Cheung
Materials Engineering
An alloy was fabricated with Ti-6Al-4V and Nb powder using laser deposition (LD) to form a compositional gradient. The gradient was deposited, starting with Ti-6Al-4V powder, onto a forged Ti-6Al-4V substrate in an Argon environment. Niobium (Nb) composition increased by 4-at.% with each layer deposited until the composition reached 100-at.% Nb. This process yielded steep thermal gradients and affected the microstructure and mechanical properties across the compositional gradient. To observe the microstructural changes in the alloy, an etched gradient was viewed with optical microscopy at 1000x, where the grain structure was observed to be an acicular α phase at 100-at.% …