Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel is currently in regular use as an alternative fuel over conventional petroleum diesel. However, corrosion of automotive materials is one of the concerns related to biodiesel compatibility issues. In addition, auto-oxidation of biodiesel can also enhance the corrosiveness of biodiesel. The present study aims to investigate inhibition effect of ethylenediamine (EDA), n-butylamine (nBA), tert-butylamine (TBA) against corrosion of cast iron. Static immersion tests in biodiesel in the presence (100 ppm) and absence of different corrosion inhibitors were carried out at room temperature for 1200 hours. At the end of the test, corrosion characteristic was investigated by weight loss measurements …
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel is currently in regular use as an alternative fuel over conventional petroleum diesel. However, corrosion of automotive materials is one of the concerns related to biodiesel compatibility issues. In addition, auto-oxidation of biodiesel can also enhance the corrosiveness of biodiesel. The present study aims to investigate inhibition effect of ethylenediamine (EDA), n-butylamine (nBA), tert-butylamine (TBA) against corrosion of cast iron. Static immersion tests in biodiesel in the presence (100 ppm) and absence of different corrosion inhibitors were carried out at room temperature for 1200 hours. At the end of the test, corrosion characteristic was investigated by weight loss measurements …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …
Study Of The Wear Behaviour Of Al-4.5% Cu-3.4% Fe In Situ Composite: Effect Of Thermal And Mechanical Processing
A.S. Md Abdul Haseeb
Wear behaviour of as-cast and heat-treated spheroidal graphite (SG) cast iron has been studied under dry sliding conditions using a pin-on-disc type apparatus. Wear tests were carried out at a linear sliding speed of 0.88 m s -1, under a constant load of 1.5 kg. All tests were performed in ambient air at room temperature. Extent of wear damage and wear mechanisms were investigated by means of weight loss measurement, optical microscopy, microhardness measurement and X-ray diffractometry on wear debris. The wear rate measured after 9500 m of sliding is found to be about three times higher in the as-cast …