Coke Degradation Under Simulated Blast Furnace Conditions, Xing Xing, Harold P. Rogers, Guangqing Zhang, Kim Hockings, Paul Zulli, Oleg Ostrovski

Faculty of Engineering and Information Sciences - Papers: Part A

Three metallurgical cokes made from coking coals over a significant range in rank were subjected to treatment with blast furnace-like gas composition-temperature profile to 1 673 K, annealing under N2 to 2 273 K and gasification with subsequent annealing at 1 873 and 2 273 K. The degradation of cokes after reaction and annealing was characterised using I-drum tumbling, tensile testing, ultra-micro indentation and X-ray diffraction. Both gasification and annealing decreased the mechanical strength of coke. Compared with annealing at 1 673 K, gasification at same temperature caused larger degradation for all three cokes, and the effect was more significant …