Effect Of Different Implant Materials On Stresses Transmitted To Peri-Implant Areas Of Implant-Retained Mandibular Overdenture, Diaa Mohamed Zahran Future University In Egypt, Diaa.Zahran@Fue.Edu.Eg, Aya Fawzy Associate Professor Of Prosthodontics, Future University In Egypt, A.Mohamed@Fue.Edu.Eg, Salah Hegazy Professor Of Prosthodontics, Faculty Of Dentistry, Mansoura University, Salahhegazy2003@Yahoo.Com, Sara M. Shabaan Lecturer At Removable Prosthodontic Department, Faculty Of Oral And Dental Medicine , Badr University, Cairo, Egypt, Ahmed A.Elwahed Shaaban Associate Professor Of Prosthodontics, Future University In Egypt, Ahmed.Abdelwahed@Fue.Edu.Eg

Future Dental Journal

Aim this in vitro study was conducted to evaluate the effect of mechanical loading on different implant materials on supporting structures materials and methods: a total of three implant retained overdentures were used in this study, retained by two implants each (Titanium, polyetheretherketon and zirconia) were placed in epoxy resin casts at the canine area using a surgical guide. Soft liner material was used at the distal extension area to mimic the soft tissues. Two linear strain gauges were bonded buccal and lingual to each implant to measure the peri-implant strains during unilateral and bilateral loading. Results: during bilateral loading …

Distal Cantilever Length Comparison In Esthetic Material For Hybrid Implant Prosthesis: An In Vitro Study., Sana Shams Eddin, Elie Jasser, Mohammad Chams Eddin, Carole Abi Ghosn Yared, Joseph Makzoumi, Paul Boulos

International Arab Journal of Dentistry

Objective: the assessment of distal cantilever length in implant supported infrastructure by comparing the load to fracture in two different framework esthetic materials (Zirconia and Polyetheretherketone (PEEK)) with two different cantilevers loading distances (10mm, 15mm). Material and methods: 20 frameworks were fabricated and divided into 4 groups (n=5): according to the material type Peek, zirconia, and according to the cantilever loading distance (10), or (15) mm and a load-to-fracture test was used until complete fracture of specimens occurs. Results: The effect of material type and cantilever loading distance were statistically significant for the mean load-to-fracture values (P< 0.05). The Zirconia group failed at higher fracture loads (817 N) than the Peek one (651 N). Frameworks with 10 mm cantilever loading distance failed at higher fracture loads than specimens with 15 mm. Conclusion: Peek is a suitable material for all-on-four framework reconstruction in specific situations, and there is a higher success rate when the distal cantilever length is kept at minimal value (10mm).

Evaluation Of Color Difference And Translucency Of Modified Peek Restorations Veneered With Different Veneering Materials Before And After Thermal Cycling, Mohamed Hamdy Abdulmaguied, Tarek Salah Morsi, Mennatallah M. Wahba, Hesham Katamish

Future Dental Journal

Objective: The aim of this study was to investigate the effect of different PEEK veneering materials, as well as thermocycling on the color difference (ΔE) and the translucency parameter (TP) of modified PEEK veneered restorations.

Materials and Methods: Thirty disc shaped specimens of veneered BioHPP (1.5 mm X 12 mm) were randomly divided into three groups (n=10) based on the type of the veneering material. Group (A): Discs veneered with CAD milled Lithium Disilicate, group (B): Discs veneered with pre-cured milled composite, and group (C): Discs veneered with conventional light cured composite. CIELab values were calculated for all specimens over …

Effect Of Different Surface Treatments And Application Times On Shear Bond Strength Between Polyetheretherketone And Composite Resin, Alper Ozdogan, Basak Topdagi

Journal of Dentistry Indonesia

Objective: To investigate the effect of various surface treatments and different application times on shear bond strength between polyetheretherketone and composite resin. Methods: A total of 110 disc-shaped polyetheretherketone specimens were randomly divided into 9 groups and 4 different surface treatments (control, sandblasting, tribochemical silica coating, sulfuric acid) were applied. The sandblasting, tribochemical silica coating, and sulfuric acid processes were performed 3 different times (10s, 15s, 20s). Then, the composite resins were applied to the treated surfaces of the polyetheretherketone specimens. The shear bond strength test and scanning electron microscopy analysis were performed. The data were statistically analyzed using …

Evaluation Of Strength Of Different Resin Materials Used In Overdenture, Mohamed Emam, Hesham E. Alam El Deen, Hamdy Abu El Fotoh, Ayman Fateen

Future Dental Journal

Introduction: Finding a suitable material that could be used to restore relatively small inter-arch spaces in which reasonable aesthetics as well as good functional strength could be achieved is a difficult process that requires good understanding of the clinical situation and precise management. Historically Metal used to offer the smallest possible thickness with excellent strength but lacks resiliency with poor aesthetics.

Aim of the study: This In-vitro study was conducted to compare two different aesthetic materials PEEK and ACETAL regarding their mechanical strength when used as Overdenture framework in a relatively small thickness.

Material and Methods: 120 specimens were …