The Causes Of Armature Surface Fracturing Within Helical Flux-Compression Generators, Jason Baird, Paul Nicholas Worsey

Mining Engineering Faculty Research & Creative Works

Aluminum and copper tubes filled with explosive were tested during this study of high strain rate effects, as an adjunct to helical flux-compression generator research at the University of Missouri-Rolla, directly affecting the understanding of flux cutoff and high strain-rate changes in generator armatures. Longitudinal cracks characteristically developed in the outer surface of armatures at a smaller expansion ratio than predicted. These cracks occurred within two diameters of the detonator end of the armature but did not extend when the tubing expanded under explosive pressurization. Such cracks appear to cause magnetic flux cutoff, and flux losses seriously affect energy conversion …