Nanoindentation Characterization On Local Plastic Response Of Ti-6al-4v Under High-Load Spherical Indentation, Yan Wen, Lechun Xie, Zhou Wang, Liqiang Wang, Weijie Lu, Laichang Zhang
Nanoindentation Characterization On Local Plastic Response Of Ti-6al-4v Under High-Load Spherical Indentation, Yan Wen, Lechun Xie, Zhou Wang, Liqiang Wang, Weijie Lu, Laichang Zhang
Research outputs 2014 to 2021
After high-load spherical indentation treatment, the variations of hardness on the plastic zone of Ti-6Al-4V were investigated via nanoindentation method. The hardness within the center of plastic zone was measured by nanoindenter, and the magnitude decreased gradually along the depth, which were caused by the different extent of plastic deformation under the residual imprint. The microstructure of indentation were observed using scanning electron microscope (SEM) before and after surface etching, and the results showed that the microhardness revealed the average hardness of α and β phases of Ti-6Al-4V. The maximum hardness reached 6.438 GPa in the depth of 132 μm. …
Beta-Type Ti-Nb-Zr-Cr Alloys With Large Plasticity And Significant Strain Hardening, Syed F. Jawed, Chirag D. Rabadia, Y. J. Liu, L. Q. Wang, Y. H. Li, X. H. Zang, Laichang C. Zhang
Beta-Type Ti-Nb-Zr-Cr Alloys With Large Plasticity And Significant Strain Hardening, Syed F. Jawed, Chirag D. Rabadia, Y. J. Liu, L. Q. Wang, Y. H. Li, X. H. Zang, Laichang C. Zhang
Research outputs 2014 to 2021
A series of Ti-25Nb-8Zr-xCr (x = 0, 2, 4, 6, 8 wt%) alloys were designed based on DV-Xα cluster method and e=a-Δr diagram with an anticipation to obtain high plasticity and significant strain hardening. The designed alloys were produced through cold crucible levitation melting technique in order to effectively investigate their micro-structures and mechanical properties. The addition of Cr significantly enhances the β stability in the microstructures of the Ti-25Nb-8Zr-xCr alloys. Both yield strength and hardness of the studied alloys increase due to the effect of solid-solution strengthening. By contrast, the plasticity, maximum strength and strain hardening rate are influenced …
Particle Size-Dependent Microstructure, Hardness And Electrochemical Corrosion Behavior Of Atmospheric Plasma Sprayed Nicrbsi Coatings, Peng Sang, Liang-Yu Chen, Cuihua Zhao, Ze-Xin Wang, Haiyang Wang, Sheng Lu, Dongpo Song, Jia-Huan Xu, Lai-Chang Zhang
Particle Size-Dependent Microstructure, Hardness And Electrochemical Corrosion Behavior Of Atmospheric Plasma Sprayed Nicrbsi Coatings, Peng Sang, Liang-Yu Chen, Cuihua Zhao, Ze-Xin Wang, Haiyang Wang, Sheng Lu, Dongpo Song, Jia-Huan Xu, Lai-Chang Zhang
Research outputs 2014 to 2021
Particle size is a critical consideration for many powder coating-related industries since it significantly influences the properties of the produced materials. However, the effect of particle size on the characteristics of plasma sprayed NiCrBSi coatings is not well understood. This work investigates the microstructures, hardness and electrochemical corrosion behavior of plasma sprayed NiCrBSi coatings synthesized using different-sized powders. All coatings mainly consist of Ni, N3B, CrB, Cr7C3 and Cr3C2 phases. The coatings produced by small particles (50–75 μm) exhibit lower porosity (2.0 ± 0.8%). Such coatings show a higher fraction (15.5 vol.%) of the amorphous phase and lower hardness (700 …