Compressive Properties Of Zone-Directionally Solidified Β-Nial And Its Off-Eutectic Alloys With Chromium And Tungsten, R. Asthana, R. Tiwari, Surendra N. Tewari
Compressive Properties Of Zone-Directionally Solidified Β-Nial And Its Off-Eutectic Alloys With Chromium And Tungsten, R. Asthana, R. Tiwari, Surendra N. Tewari
Chemical & Biomedical Engineering Faculty Publications
The ordered intermetallic compound β-NiAl and its pseudo-binary off-eutectic alloys with 1 at.% tungsten and 9.7 at.% chromium were directionally solidified (DS) in the ‘floating-zone’ mode, and tested for compressive strength and fracture behavior in the temperature range 300–800 K. The dual-phase structures created by the DS of ternary NiAl alloys led to improvements in both the compressive strength and the ductility. The room-temperature (300 K) 0.2% compressive yield strength (CYS) of DS NiAl(W) (623 MPa) is larger than the CYS of DS NiAl(Cr) (565 MPa) and DS NiAl (435 MPa). The CYS of the three alloys dropped …
Design Of Durable Concrete Railroad Crossings, Anthony J. Lamanna, Charles F. Scholer
Design Of Durable Concrete Railroad Crossings, Anthony J. Lamanna, Charles F. Scholer
JTRP Technical Reports
Existing precast concrete railroad crossings in the state of Indiana are experiencing too short a life expectancy. This study proposes methods that can be used to produce durable concrete railroad crossings with satisfactory rideability, durability, and longevity. Thirty-two precast concrete railroad crossings were visited in central and northern Indiana. Failures were determined to belong to three major categories: structural capacity causes, environmental causes, and material property causes. A concrete mix was evaluated at three different polyolefin fiber contents and without fibers. Beams were tested in flexure, and modulus of rupture and first crack deflection were recorded for each beam. Cylinders …