Crystal And Electronic Structures Of The Complex Hydride Li₄Bn₃H₁₀, Jinbo Yang, X. J. Wang, Qingsheng Cai, William B. Yelon, William Joseph James
Crystal And Electronic Structures Of The Complex Hydride Li₄Bn₃H₁₀, Jinbo Yang, X. J. Wang, Qingsheng Cai, William B. Yelon, William Joseph James
Physics Faculty Research & Creative Works
The crystal structure of Li4BN3H10 was investigated using powder neutron diffraction with high sensitivity. The compound crystallizes in the cubic space group 213 with lattice parameters a=10.645 19(52) Å with an ordered arrangement of [NH2]−1 and [BH4]−1 anions in a molar ratio of 3:1. The bond lengths between the nearest nitrogen and hydrogen atoms are 1.04(4) and 1.14(4) Å. The bond angle between H(1)-N-H(2) is about 126(6)°, while those between H(3)-B-H(3) and H(3)-B-H(4) are about 109(6)°-110(7)°. There are three different Li sites surrounded by [NH2]−1 and [BH4]−1 anions in distorted tetrahedral configurations. The Li(3)-B and Li(3)-N bond distances are about …
Structure, Magnetic, And Transport Properties Of Ti-Substituted La₀.₇Sr₀.₃Mno₃, M. S. Kim, Jinbo Yang, Qingsheng Cai, X.-D. Zhou, William Joseph James, William B. Yelon, D. Buddhikot, Satish K. Malik, Paul Ernest Parris
Structure, Magnetic, And Transport Properties Of Ti-Substituted La₀.₇Sr₀.₃Mno₃, M. S. Kim, Jinbo Yang, Qingsheng Cai, X.-D. Zhou, William Joseph James, William B. Yelon, D. Buddhikot, Satish K. Malik, Paul Ernest Parris
Materials Science and Engineering Faculty Research & Creative Works
Ti-substituted perovskites La0.7Sr0.3Mn1-xTixO3 with 0 ≤ x ≤ 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a,c and the unit cell volume increase with increasing Ti content. However, at 10 K, the cell parameter a has a maximum value for x = 0.10, and decreases for x > 0.10, while the unit cell volume remains nearly constant for x > 0.10. The average (Mn,Ti)-O bond length increases …