Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The beneficial effects of Si on both the metallurgical and corrosion properties of Cr-Mo steels have previously been demonstrated at UNLV. Therefore, additions of Si ranging from 0.5-2.0 weight percent (wt%) was attempted in this investigation to explore Si effect on both the high temperature tensile properties and corrosion behavior of T91 grade steel. Corrosion studies in the presence of molten LBE could not be performed due to a lack of proper experimental facilities at UNLV. Therefore, detailed corrosion studies involving Si-containing T91 grade steels were performed in an aggressive aqueous solution of acidic pH. Further, significant efforts have been …

Effect Of Silicon Content On The Corrosion Resistance And Radiation- Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

This task is focused on the evaluation of the effects of silicon content on both the corrosion behavior and radiation-induced embrittlement of martensitic stainless steels having compositions similar to that of modified 9Cr-1Mo steel, also known as T91 grade steel. T91 grade steel was selected to be a candidate structural material to contain molten lead-bismuth eutectic (LBE), which can act both as a target material and a coolant during the spallation process. The operating temperature during this process may range from 420-550 °C. Thus, moderate tensile strength of the containment material (T91) is a major requirement.

The beneficial effects of …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems: Quarterly Progress Report (November 2005 – January 2006), Ajit K. Roy

Transmutation Sciences Materials (TRP)

This task is intended to study the effect of Si content not only on the corrosion resistance but also on the radiation-induced embrittlement of martensitic stainless steels. The susceptibility of these alloys with different Si content to stress corrosion cracking, general corrosion and localized corrosion will be evaluated in the molten LBE and aqueous environments of different pH values using state-of-the-art testing techniques. Testing in the aqueous media is intended to develop baseline data for comparison purpose. Radiation-induced embrittlement of these alloys will initially be studied by irradiating the test specimens with bremmstrahlung gamma radiation from 20-40 MeV electron beams …

Effect Of Silicon Content On The Corrosion Resistance And Radiation- Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

This task is primarily focused on the evaluation of the effect of Si content on the susceptibility of modified 9Cr-1Mo-0.24V steel to stress corrosion cracking (SCC) and localized cracking in both molten lead-bismuth eutectic (LBE) and an aqueous solution of acidic pH.

Further, significant efforts are in progress to characterize the deformation mechanism of modified T91 grade steel as a function of temperature and strain rate. Simultaneously, surface analyses of the tested materials are ongoing using state-of-the-art techniques including scanning electron microscopy (SEM) and transmission electron microscopy (TEM).

Cracking Of Martensitic Alloy Ep-823 Under Controlled Potential, Ajit K. Roy, M. K. Hossain

Mechanical Engineering Faculty Research

The susceptibility of martensitic Alloy EP-823 to stress corrosion cracking was evaluated with and without an applied cathodic potential using the slow-strain-rate (SSR) testing technique. The magnitude of the applied potential was based on the corrosion potential determined by cyclic polarization. The cracking susceptibility in an acidic environment at different temperatures was expressed in terms of the true failure stress (ơ_f), time to failure (TTF), and ductility parameters, including percent elongation (%El) and percent reduction in area (%RA). The data indicate that the magnitudes of ơ_r, TTF, %El, and %RA were reduced due to cathodic charging. …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems: Quarterly Progress Report (February – April 2005), Ajit K. Roy

Transmutation Sciences Materials (TRP)

This proposal is intended to study the effect of Si content not only on the corrosion resistance but also on the radiation-induced embrittlement of martensitic stainless steels. The susceptibility of these alloys with different Si content to stress corrosion cracking, general corrosion and localized corrosion will be evaluated in the molten LBE and aqueous environments of different pH values using state-of-the-art testing techniques. Testing in the aqueous media is intended to develop baseline data for comparison purpose. Radiation-induced embrittlement of these alloys will initially be studied by irradiating the test specimens with bremmstrahlung gamma radiation from 20-40 MeV electron beams …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems: Quarterly Progress Report (November 2004 – January 2005), Ajit K. Roy

Transmutation Sciences Materials (TRP)

This proposal is intended to study the effect of Si content not only on the corrosion resistance but also on the radiation-induced embrittlement of martensitic stainless steels. The susceptibility of these alloys with different Si content to stress corrosion cracking, general corrosion and localized corrosion will be evaluated in the molten LBE and aqueous environments of different pH values using state-of-the-art testing techniques. Testing in the aqueous media is intended to develop baseline data for comparison purpose. Radiation-induced embrittlement of these alloys will initially be studied by irradiating the test specimens with bremmstrahlung gamma radiation from 20-40 MeV electron beams …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems: Quarterly Progress Report (August 2004 – October 2004), Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada Las Vegas (UNLV), Los Alamos National Laboratory (LANL) and Idaho State University (ISU) is to evaluate the effect of silicon (Si) content on the corrosion behavior and radiation-induced embrittlement of martensitic stainless steels having chemical compositions similar to that of the modified 9Cr-1Mo steel. Recent studies at LANL involving Alloy EP-823 of different Si content have demonstrated that increased Si content in this alloy may enhance the corrosion resistance in molten lead-bismutheutectic (LBE). Since very little data exists in the open literature on the beneficial effect of Si …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The primary objective of this task was to evaluate the effects of environmental and mechanical parameters on environment induced degradations of candidate target structural materials for applications in spallation-neutron-target systems. The materials selected for evaluation and characterization were martensitic stainless steels including Alloys HT-9, EP-823, and 422.

Accelerator-driven transmutation systems involve bombarding a target material such as molten lead-bismuth-eutectic (LBE) by a proton beam, thereby producing neutrons. The molten LBE target will be contained in a subsystem structural container made of a suitable material such as Alloys HT-9, EP-823, and 422. During the transmutation process, the target structural material may …

Effect Of Silicon Content On The Corrosion Resistance And Radiation- Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

This task is focused on the evaluation of the effect of Si content on the corrosion behavior and radiation-induced embrittlement of martensitic steels having chemical compositions similar to that of modified 9Cr-1Mo steel. Numerous state-of-the-art experimental techniques are currently being planned to be employed to achieve the desired research goal.

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Annual Progress Report (May 2003 – May 2004), Ajit K. Roy

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task was to evaluate the effect of hydrogen on environment-assisted cracking of candidate target structural materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization were martensitic stainless steels including Alloy EP 823, HT-9, and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) of these materials were evaluated in neutral and acidic aqueous environments using smooth and notched tensile specimens under constant-load (CL) and slow-strain-rate (SSR) conditions. Further, the …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada Las Vegas (UNLV), Los Alamos National Laboratory (LANL) and Idaho State University (ISU) is to evaluate the effect of silicon (Si) content on the corrosion behavior and radiation-induced embrittlement of martensitic stainless steels having chemical compositions similar to that of the modified 9Cr-1Mo 2 steel. Recent studies at LANL involving Alloy EP-823 of different Si content have demonstrated that increased Si content in this alloy may enhance the corrosion resistance in molten lead-bismuth-eutectic (LBE). Since very little data exists in the open literature on the beneficial effect of …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of environmental and mechanical parameters on environment induced degradations of candidate target structural materials for applications in spallation-neutron-target systems, such as accelerator-driven systems for the transmutation of waste. The materials selected for evaluation and characterization are martensitic stainless steels including Alloys HT-9, EP-823 and Type 422 stainless steel (SS).

More recently, this experimental program has been expanded to evaluate the effect of molten lead-bismuth eutectic (LBE) on the corrosion behavior of target structural materials in the presence of oxygen. Since the Materials Performance Laboratory (MPL) at UNLV currently cannot …

Stress Corrosion Cracking Of Target Material, Mohammad K. Hossain

Transmutation Sciences Materials (TRP)

The primary objective of this paper is to evaluate the effect of hydrogen on environment assisted cracking of candidate target materials for transmutation applications. Transmutation refers to transformation of long-lived actinides and fission products from spent nuclear fuels (SNF), and occurs when the nucleus of an atom changes because of natural radioactive decay, nuclear fission, nuclear fusion, neutron capture, or other related processes. Martensitic Alloy EP 823 was selected to be the candidate alloy for this investigation. During the initial phase, the stress corrosion cracking (SCC) behavior of this alloy was evaluated in neutral (pH: 6-7) and acidic (pH: 2-3) …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Quarterly Progress Report (June 1 – August 31, 2003), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallationneutron- target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in aqueous environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Annual Progress Report (May 2002 – May 2003), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallationneutron- target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in aqueous environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. …

Stress Corrosion Cracking Of Type 422 Stainless Steel For Applications In Spallation-Neutron-Target Systems, Ramprashad Prabhakaran

Transmutation Sciences Materials (TRP)

Introduction

• This research program is aimed at evaluating different types of environment-induced degradation of candidate target materials for applications in transmutation of spent nuclear fuels (SNF).

• Transmutation refers to the elimination of long-lived actinides and fission products from SNF.

Objectives

• Evaluate susceptibility of candidate target materials to stress corrosion cracking (SCC) and localized corrosion (pitting and crevice) in neutral and acidic aqueous environments at ambient and elevated temperatures

• Determine the extent and morphology of cracking in tested materials as functions of experimental and environmental variables including pH, temperature, loading conditions and specimen geometry

• Develop mechanistic …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

During the past two years (2001-2002) of this project, the primary effort was focused on evaluating the effect of hydrogen on the cracking behavior of candidate target materials namely, Alloys EP-823, HT-9 and 422 in aqueous environments of different pH values at ambient and elevated temperatures. More recently, emphasis is being placed to evaluate the cracking behavior of these materials in molten lead-bismuth eutectic (LBE) environment at much higher testing temperatures so as to compare the cracking susceptibility in environments containing molten metals and aqueous solutions, respectively. The most recent tests to evaluate the cracking susceptibility were primarily based on …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy, Brendan O'Toole, Zhiyong Wang, David W. Hatchett

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the potential for the environmentally-assisted cracking of candidate target materials for applications in spallation-neutron-target systems, such as accelerator-driven system for the transmutation of waste. The materials selected for evaluation and characterization are martensitic stainless steels (SS) including Alloys HT- 9, EP 823 and Type 422 stainless steel.

More recently, this experimental program has been expanded to evaluate the effect of molten lead-bismuth eutectic (LBE) on the corrosion behavior of target materials in the presence of oxygen. Since the materials performance laboratory (MPL) at UNLV currently cannot accommodate this type of testing, …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems: Quarterly Progress Report (June 01 – August 31, 2002), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. Further, the localized corrosion behavior of these alloys …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems: Annual Progress Report (May 2001 – May 2002), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. Further, the localized corrosion behavior of these alloys …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Aaa Task-4 Quarterly (December 1, 2001 – February 28, 2002) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including HT- 9, EP 823 and 422. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these alloys will be evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. The extent and morphology of cracking of these alloys will further be evaluated …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The purpose of this project is to evaluate the effect of hydrogen on cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The test materials will undergo appropriate thermal treatments prior to being hydrogen-charged by potentiostatic cathodic polarization technique in a simulated aqueous environment at different temperatures of interest. The specimens, upon completion of testing, will be metallographically examined. Further, the scanning electron microscopy (SEM) will be used to determine the extent and nature of cracking in the specimens tested. The thrust of the proposed …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems, Ajit K. Roy, Brendan O'Toole, Zhiyong Wang, David W. Hatchett

Transmutation Sciences Materials (TRP)

Spallation-neutron-sources, such as those under investigation for use in accelerator-driven transmutation systems, generate neutrons through the collision of high-energy protons, or charged hydrogen atoms, with heavy metal targets such as lead. As a result, these systems also tend to deposit a significant amount of hydrogen in the materials of the transmuter target and superstructure. This can result in accelerated corrosion and changes in the properties of the exposed materials. Of particular importance is a phenomenon called hydrogen embrittlement, in which materials lose their ductility (ability to deform under stress) and become brittle (more susceptible to fracture) after reacting with hydrogen. …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Aaa Task-4 Quarterly (September 1 – November 30, 2001) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including HT- 9, EP 823 and 422. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these alloys will be evaluated in environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. The extent and morphology of cracking of these alloys will further be evaluated …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Aaa Task-4 Quarterly (June 1 – August 31, 2001) Report, Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

The subject task entitled “Hydrogen-Induced Embrittlement of Candidate Target Materials for Applications in Spallation-Neutron-Target Systems” had commenced during the quarter ending on August 31, 2001. A research account has been established, contracts for both faculty and students have been prepared, and efforts are well underway to embark on the related research activities, as proposed.

As the title of this project implies, the primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate materials for applications in spallationneutron- target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). …

Hydrogen-Induced Embrittlement Of Candidate Target Materials For Applications In Spallation-Neutron-Target Systems, Brendan O'Toole, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this project is to evaluate the effect of hydrogen on cracking of candidate target materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The test materials will undergo appropriate thermal treatments prior to being hydrogen-charged by potentiostatic cathodic polarization technique in a simulated aqueous environment at different temperatures of interest. The specimens, upon completion of testing, will be metallographically examined. Further, the scanning electron microscopy (SEM) will be used to determine the extent and nature of cracking in the specimens tested. The thrust of the proposed …