Theoretical Modeling Of Protective Oxide Layer Growth In Non-Isothermal Lead Alloy Coolant Systems, Yitung Chen, Jinsuo Zhang, Huajun Chen, Jichun Li

Transmutation Sciences Materials (TRP)

In advanced nuclear energy systems, lead-alloys (e.g., lead, lead bismuth eutectic) emerge as strong candidates for transmutation and advanced reactor systems as nuclear coolants and high-power spallation neutron targets. However, it is widely recognized that corrosion of materials caused by lead-alloys presents a critical barrier to their industrial use. A few experimental research and development projects have been set up by different groups such as LANL to study the corrosion phenomena in their test facilities and to develop mitigation techniques and materials.

The goal of the proposed research project is to provide basic understanding of the protective oxide layer behaviors …

Corrosion Barrier Development For Lbe Corrosion Resistance, Biswajit Das

Transmutation Sciences Materials (TRP)

In the last quarter, a specialized sample holder was developed for the anodization of alumina on steel. In addition, it was determined that oxalic acid was the most appropriate acid for the anodization of these structures. The steel samples obtained from LANL were first cut into a number of pieces, each measuring 11mm x 8mm x 1.6mm, to allow multiple experiments. Special care was taken to ensure that the cutting process did not damage the samples. After investigation of several techniques, including laser cutting, the samples were cut using EDM wires. The cut steel pieces did not show any damage …

Corrosion Barrier Development For Lbe Corrosion Resistance: Quaterly Report, Biswajit Das

Transmutation Sciences Materials (TRP)

With the demonstration of formation of nanoporous alumina on steel and its good adhesion to substrate under thermal cycling, the next project task was to synthesize Chromium nanowires inside the alumina pores. During the previous quarter, a specialized sample holder was developed towards this goal. Various techniques for the deposition of Chromium were investigated and electro-deposition was determined to be the most suitable approach due to the large aspect ratio of the pores. A challenge in using electro-deposition for porous alumina is the potential sealing of the pores in aqueous solutions at higher temperatures. To avoid this problem, a search …

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications, Biswajit Das

Transmutation Sciences Materials (TRP)

Advanced transmutation systems require structural materials that are able to withstand high neutron fluxes, high thermal cycling, and high resistance to chemical corrosion. The current candidate materials for such structures are ferritic and ferritic-martensitic steels due to their strong resistance to swelling, good microstructural stability under irradiation, and the retention of adequate ductility at typical reactor operating temperatures.

In parallel, lead bismuth eutectic (LBE) has emerged as a potential spallation target material for efficient production of neutrons, as well as a coolant in the accelerator system. While LBE has excellent properties as a nuclear coolant, it is also highly corrosive …

Theoretical Modeling Of Protective Oxide Layer Growth In Non-Isothermal Lead-Alloys Coolant Systems, Yitung Chen

Transmutation Sciences Materials (TRP)

The goal of the proposed research project is to provide basic understanding of the protective oxide layer behaviors and to develop oxide layer growth models of steels in non-isothermal lead-alloys (lead or lead-bismuth eutectic) coolant systems. It is widely recognized that the corrosiveness of the lead-alloys is a critical obstacle and challenge for which it can be safely used or applied in the nuclear coolant systems. Active oxygen control technique can promote the formation of the “self-healing” oxide films on the structural material surface, drastically reducing steel corrosion and coolant contamination. Many experiments of steels exposed to flowing lead-alloys have …

Fundamental And Applied Experimental Investigations Of Corrosion Of Steel By Lbe Under Controlled Conditions: Kinetics, Chemistry, Morphology, And Surface Preparation: Quarterly Report (October-December 2004), Allen L. Johnson, John Farley, Dale L. Perry

Transmutation Sciences Materials (TRP)

This project has four components:

(1) the fabrication of a materials test apparatus with unique capabilities,

(2) comparative studies of steel corrosion under gas phase conditions comparable to the Lead Bismuth Eutectic (LBE) oxygen control conditions,

(3) isotope labeling studies, and

(4) collaborative efforts with other workers in the field.

Cfd Analysis Of 3-D Thermalhydraulics Flow Effects On Wall Concentration Gradient Profiles For Lbe Loop Fittings, Narain Armbya

UNLV Theses, Dissertations, Professional Papers, and Capstones

The objective of the thesis is to study the effects of thermalhydraulics flows on the wall concentration gradient profiles in LBE loop fittings. To that end detailed models of the fittings have been constructed to study these effects. These fittings include sudden expansion, sudden contraction, t-joint and elbow. The typical flow rates chosen for these simulations are typical of design criteria chosen for the loop with Reynolds numbers expected around 200,000 and the usual axial temperature profiles which are being characterized in the DELTA loop at LANL. STAR-CD is the simulation package used to make these predictions, which include detailed …

Developing A Sensing System For The Measurement Of Oxygen Concentration In Liquid Pb-Bi Eutectic: Quarterly Progress Report (July 1 – Sept. 30, 2004), Yingtao Jiang, Bingmei Fu

Transmutation Sciences Materials (TRP)

Dr. Jiang Ma and Mr. Xiaolong Wu worked in LANL between July 1 and Sept. 15 to conduct the experiment. Test of the corrosion of different materials in LBE was performed. The influence of the process of gas introduction to the LBE was studied. Data analysis work was performed based on accumulated data. In the same time, progress has been made in the simulation for transport in oxygen mixing, and one paper was presented in a conference. Another paper was composed and submitted to IEEE International Symposium of Circuits and Systems for the track Chemical Sensors. Preparation of a paper …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Trp Final Report 09/01/2003-08/31/2004, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Fourth Quarterly Report 06/01/2004-08/31/2004, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Annual Progress Report (May 2003 – May 2004), Ajit K. Roy

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task was to evaluate the effect of hydrogen on environment-assisted cracking of candidate target structural materials for applications in spallation-neutron-target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization were martensitic stainless steels including Alloy EP 823, HT-9, and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) of these materials were evaluated in neutral and acidic aqueous environments using smooth and notched tensile specimens under constant-load (CL) and slow-strain-rate (SSR) conditions. Further, the …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Third Quarterly Report 03/01/2004-05/31/2004, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications, Biswajit Das

Transmutation Sciences Materials (TRP)

The objective of this project is to develop a novel nanostructure based coating technology that will provide significantly improved corrosion resistance for steel in LBE at elevated temperatures (500 - 600^oC), as well as provide long-term reliability under thermal cycling. The nanostructure based coatings will consist of a layer of nanoporous alumina with the pores filled with an oxidizing metal such as Cr, followed by a capping layer of alumina. Alumina, which is a robust anti-corrosion material, provides corrosion resistance at elevated temperatures. The Cr serves two purposes: (1) it acts as a solid filler material for the …

Effect Of Silicon Content On The Corrosion Resistance And Radiation-Induced Embrittlement Of Materials For Advanced Heavy Liquid Metal Nuclear Systems, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada Las Vegas (UNLV), Los Alamos National Laboratory (LANL) and Idaho State University (ISU) is to evaluate the effect of silicon (Si) content on the corrosion behavior and radiation-induced embrittlement of martensitic stainless steels having chemical compositions similar to that of the modified 9Cr-1Mo 2 steel. Recent studies at LANL involving Alloy EP-823 of different Si content have demonstrated that increased Si content in this alloy may enhance the corrosion resistance in molten lead-bismuth-eutectic (LBE). Since very little data exists in the open literature on the beneficial effect of …

Theoretical Modeling Of Protective Oxide Layer Growth In Non-Isothermal Lead-Alloys Coolant Systems, Yitung Chen, Jinsuo Zhang, Jichun Li

Transmutation Sciences Materials (TRP)

The goal of the proposed research project is to provide basic understanding of the protective oxide layer behaviors and to develop oxide layer growth models of steels in non-isothermal leadalloys (lead or lead-bismuth eutectic) coolant systems. It is widely recognized that the corrosiveness of the lead-alloys is a critical obstacle and challenge for which it can be safely used or applied in the nuclear coolant systems. Active oxygen control technique can promote the formation of the “self-healing” oxide films on the structural material surface, drastically reducing steel corrosion and coolant contamination. Many experiments of steels exposed to flowing leadalloys have …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: First Quarterly Report 01/12/04-02/29/04, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Corrosion Of Steel By Lead Bismuth Eutectic, John Farley, Allen L. Johnson, Dale L. Perry

Transmutation Sciences Materials (TRP)

There is an active international interest in lead-bismuth eutectic and similar liquid lead systems because of the relevance to the transmutation of nuclear waste, fast reactors, and spallation neutron sources. A successful program in nuclear waste processing that includes transmutation in accelerator-driven systems and fast reactors, would significantly decrease the space requirements for geological repositories.

Materials in these systems must be able to tolerate high neutron fluxes, high temperatures, and chemical corrosion. For lead bismuth eutectic (LBE) systems, there is an additional challenge because the corrosive behaviors of materials in LBE are not well understood. Most of the available information …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The primary objective of this task is to evaluate the effect of environmental and mechanical parameters on environment induced degradations of candidate target structural materials for applications in spallation-neutron-target systems, such as accelerator-driven systems for the transmutation of waste. The materials selected for evaluation and characterization are martensitic stainless steels including Alloys HT-9, EP-823 and Type 422 stainless steel (SS).

More recently, this experimental program has been expanded to evaluate the effect of molten lead-bismuth eutectic (LBE) on the corrosion behavior of target structural materials in the presence of oxygen. Since the Materials Performance Laboratory (MPL) at UNLV currently cannot …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The corrosion of structural materials is a major concern for the use of lead-bismuth eutectic (LBE) systems for nuclear applications such as in transmuter targets or fast reactors. Corrosion in liquid metal systems can occur through various processes, including, for example, dissolution, formation of inter-metallic compounds at the interface, and penetration of liquid metal along grain boundaries. Predicting the rate of these processes depends on numerous system operational factors: temperature, system geometry, thermal gradients, solid and liquid compositions, and velocity of the liquid metal, to name a few. Corrosion, along with mechanical and/or hydraulic factors, often contributes to component failure. …

Developing A Sensing System For The Measurement Of Oxygen Concentration In Liquid Pb-Bi Eutectic, Yingtao Jiang, Bingmei Fu, Woosoon Yim

Transmutation Sciences Materials (TRP)

Lead-bismuth eutectic (LBE) is a candidate as a spallation target in sub-critical transmutation systems and as a coolant in nuclear programs. One of the primary concerns with LBE systems is the corrosion of stainless steel, the primary structural material used in nuclear systems. To mitigate this problem, trace levels of oxygen can be introduced into the system, causing the formation of a protective oxide layer at the interface between the LBE and steel. To protect the steel components, this oxide layer must be properly maintained. However, too much oxygen will produce unwanted oxide precipitation within the coolant and elsewhere in …

Fundamental And Applied Experimental Investigations Of Corrosion Of Steel By Lbe Under Controlled Conditions: Kinetics, Chemistry, Morphology, And Surface Preparation: Quarterly Report, Allen L. Johnson, John Farley, Dale L. Perry

Transmutation Sciences Materials (TRP)

This project has four components:

(1) the fabrication of a materials test apparatus with unique capabilities,

(2) comparative studies of steel corrosion under gas phase conditions comparable to the Lead Bismuth Eutectic (LBE) oxygen control conditions,

(3) isotope labeling studies, and

(4) collaborative efforts with other workers in the field.

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications: Quaterly Report, Biswajit Das

Transmutation Sciences Materials (TRP)

During the past quarter, this project employed one graduate student and two undergraduate student researchers and made the following accomplishments :

• Acquisition of steel samples for experiments

• Design and fabrication of specialized anodization apparatus to accommodate steel samples

• Investigation of adhesiveness of aluminum on steel

• Investigation of effects of anodizing acids on steel to identify most appropriate acid and a suitable barrier material

Chemical Kinetics And Thermal Hydraulics Of Lead Bismuth Flow Loops, Kanthi Kiran Dasika

UNLV Theses, Dissertations, Professional Papers, and Capstones

The objective of the thesis is to study the effect of chemical kinetics and thermal hydraulics of Lead Bismuth Eutectic (LBE) flow in the Materials Test Loop (MTL). The Materials Test Loop, also known as the Delta Loop, was built in Los Alamos National Laboratories (LANL) to obtain the experimental data for corrosion estimation and analysis. It is a well-known fact that corrosion plays an important role in the design of nuclear thermal hydraulic systems. Since the MTL is a multi-section closed system that differs in diameter from one part to another, an intensive study on the overall and regional …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Fourth Quarterly Report 09/01/2003-11/30/2003, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Quarterly Progress Report (June 1 – August 31, 2003), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallationneutron- target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in aqueous environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Fourth Quarterly Report 06/01/2003-08/30/2003, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics-Task V: Annual Report -Phase Ii 09/01/2002-08/30/2003, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The Lead-Bismuth eutectic (LBE) has been determined from previous experimental studies by the Russians and the European scientific community to be a potential material that can be used as a spallation target and coolant for the TRP proposed application. Properly controlling the oxygen content in LBE can drastically reduce the LBE corrosion to structural steels. However, existing knowledge of material corrosion performance was obtained from point-wise testing with only very sparse experimental data. Scientists have noticed that the concentration of oxygen dissolved in the liquid alloy could control the corrosion rate of steels exposed to Pb or Pb-Bi. At high …

Modeling Corrosion In Oxygen Controlled Lbe Systems With Coupling Of Chemical Kinetics And Hydrodynamics - Phase Three, Samir Moujaes, Yitung Chen

Transmutation Sciences Materials (TRP)

The proposed work will combine chemical kinetics and hydrodynamics in target and test-loop lead-bismuth eutectic (LBE) systems to model system corrosion effects. This approach will result in a predicative tool that can be validated with corrosion test data, used to systematically design tests and interpret the results, and provide guidance for optimization in LBE system designs. The task includes two subtasks. The first subtask is to try to develop the necessary predictive tools to be able to predict the levels of oxygen and corrosion products close to the boundary layer through the use of Computational Fluid Dynamics (CFD) modeling. The …

Study Of Geometric Effects On Local Corrosion Rates For Lbe Loop, Chao Wu

UNLV Theses, Dissertations, Professional Papers, and Capstones

Corrosion is an extremely important issue in nuclear cooling system applications. Many scientific and engineering efforts have been contributed to the research of finding an ideal material, which has resistance to corrosive Lead Bismuth Eutectic (LBE). A Delta Loop was designed and constructed in Los Alamos National Lab (LANL) to obtain the experimental data. This loop is a multi-section closed system that differs in diameter from one part to another. As a result, an intensive study on the geometry effect is hence necessary and valuable. In this thesis, this problem was simulated by commercial software STAR-CD. Results provide a good …

Environment-Induced Degradation And Crack-Growth Studies Of Candidate Target Materials: Annual Progress Report (May 2002 – May 2003), Ajit K. Roy, Brendan O'Toole

Transmutation Sciences Materials (TRP)

As indicated in the original proposal, the primary objective of this task is to evaluate the effect of hydrogen on environment-assisted cracking of candidate target materials for applications in spallationneutron- target (SNT) systems such as accelerator production of tritium (APT) and accelerator transmutation of waste (ATW). The materials selected for evaluation and characterization are martensitic stainless steels including Alloy HT-9, Alloy EP 823 and Type 422 stainless steel. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of these materials are being evaluated in aqueous environments of interest using tensile specimens under constant load and slow-strain-rate (SSR) conditions. …