Crystallite Phase And Orientation Determinations Of (Mn, Ga) As/Gaas-Crystallites Using Analyzed (Precession) Electron Diffraction Patterns, Ines Häusler, Stavros Nicolopoulos, Edgar F. Rauch, K. Volz, Peter Moeck

Physics Faculty Publications and Presentations

Outline of the presentation:

1. Material system: (Mn,Ga)As/GaAs-crystallites

2. Structure analysis using Nano-beam Diffraction (NBD) Precession Electron Diffraction Technique (PED) --> Structure type I + II

3. Phase and orientation mapping using ASTAR

4. Conclusion

Automated Nanocrystal Orientation And Phase Mapping In The Transmission Electron Microscope On The Basis Of Precession Electron Diffraction, Edgar F. Rauch, Joaquin Portillo, Stavros Nicolopoulos, Daniel Bultreys, Sergei Rouvimov, Peter Moeck

Physics Faculty Publications and Presentations

An automated technique for the mapping of nanocrystal phases and orientations in a transmission electron microscope is described. It is primarily based on the projected reciprocal lattice geometry that is extracted from electron diffraction spot patterns. Precession electron diffraction patterns are especially useful for this purpose. The required hardware allows for a scanning-precession movement of the primary electron beam on the crystalline sample and can be interfaced to any older or newer mid-voltage transmission electron microscope (TEM). Experimentally obtained crystal phase and orientation maps are shown for a variety of samples. Comprehensive commercial and open-access crystallographic databases may be used …

Precession Electron Diffraction And Its Advantages For Structural Fingerprinting In The Transmission Electron Microscope, Peter Moeck, Sergei Rouvimov

Physics Faculty Publications and Presentations

The foundations of precession electron diffraction in a transmission electron microscope are outlined. A brief illustration of the fact that laboratory-based powder X-ray diffraction fingerprinting is not feasible for nanocrystals is given. A procedure for structural fingerprinting of nanocrystals on the basis of structural data that can be extracted from precession electron diffraction spot patterns is proposed.