Nanoscience and Nanotechnology Commons^™

Corrosion Barrier Development For Lbe Corrosion Resistance, Biswajit Das

Transmutation Sciences Materials (TRP)

In the last quarter, a specialized sample holder was developed for the anodization of alumina on steel. In addition, it was determined that oxalic acid was the most appropriate acid for the anodization of these structures. The steel samples obtained from LANL were first cut into a number of pieces, each measuring 11mm x 8mm x 1.6mm, to allow multiple experiments. Special care was taken to ensure that the cutting process did not damage the samples. After investigation of several techniques, including laser cutting, the samples were cut using EDM wires. The cut steel pieces did not show any damage …

Corrosion Barrier Development For Lbe Corrosion Resistance: Quaterly Report, Biswajit Das

Transmutation Sciences Materials (TRP)

With the demonstration of formation of nanoporous alumina on steel and its good adhesion to substrate under thermal cycling, the next project task was to synthesize Chromium nanowires inside the alumina pores. During the previous quarter, a specialized sample holder was developed towards this goal. Various techniques for the deposition of Chromium were investigated and electro-deposition was determined to be the most suitable approach due to the large aspect ratio of the pores. A challenge in using electro-deposition for porous alumina is the potential sealing of the pores in aqueous solutions at higher temperatures. To avoid this problem, a search …

Development Of Nanostructure Based Corrosion-Barrier Coatings On Steel For Transmutation Applications, Biswajit Das

Transmutation Sciences Materials (TRP)

Advanced transmutation systems require structural materials that are able to withstand high neutron fluxes, high thermal cycling, and high resistance to chemical corrosion. The current candidate materials for such structures are ferritic and ferritic-martensitic steels due to their strong resistance to swelling, good microstructural stability under irradiation, and the retention of adequate ductility at typical reactor operating temperatures.

In parallel, lead bismuth eutectic (LBE) has emerged as a potential spallation target material for efficient production of neutrons, as well as a coolant in the accelerator system. While LBE has excellent properties as a nuclear coolant, it is also highly corrosive …