Mechanically Activated Combustion Synthesis Of Molybdenum Borosilicides For Ultrahigh-Temperature Structural Applications, Alan Alberto Esparza Hernandez

Open Access Theses & Dissertations

The desire to improve the efficiency of power generation gas-turbines has led to a relentless quest for new, ultrahigh-temperature structural materials to replace the current nickel-based superalloys. These materials have reached the maximum allowable operating temperature determined by the melting temperature of these alloys, which is about 1150 °C. These materials could be replaced by molybdenum silicides and borosilicides based on Mo5SiB 2 (T2) phase due to their high melting point and mechanical properties. A major challenge, however, is to simultaneously achieve high oxidation resistance and acceptable mechanical properties at elevated temperatures. One novel approach to improve these properties is …

Thermal Shock Studies On Carbon-Carbon Composites: Experimentation And Analysis, Alma Lucia Leanos

Open Access Theses & Dissertations

The oxidation behavior of C/C composites under thermal shock conditions in air is understood and predicted experimentally and by computational efforts. In Chapter. 1, both compressive properties and oxidation behavior of pristine and thermal shock exposed 2D C/C composite specimens were examined. Pristine test specimens were exposed to thermal shock conditions with temperatures ranging from 400°C to 1000°C in an oxidizing environment, followed by compression tests on pristine and thermal shock exposed specimens to obtain their compressive responses.

Similarly, in Chapter. 2, the influence of thermal shock conditions on both, the extent of carbon materials decomposition and the through-thickness compressive …

Oxidation Of Borides And Carbides With Y2o3 And Ta Additions, Salvador Manuel Rodriguez

Open Access Theses & Dissertations

The study presented here describes an investigation of an oxidation scale of a fully-sintered Y2O3-ZrB2-TiC composite exposed in air at 1173K. Upon oxidation of the boride/carbide, a ZrO2-TiO2 was expected to form similar to the ZrO2-SiO2 dual scale of an oxidized ZrB2-SiC. The 47wt% Y2O3-38wt%ZrB2-16wt%TiC composite formed a dual scale consisting primarily of an Y2O3-ZrO2-TiC inner scale with an outer scale of ZrO2-TiO2-Y2O3.

The samples oxidized with a parabolic layer growth allowing the calculation of the effective diffusion coefficient indicating that the oxidation was controlled by oxygen ingress through primarily the ZrO2-Y2O3 phase. The oxygen potential between the inner layer …