Nanofatigue Studies Of Ultrathin Hard Carbon Overcoats Used In Magnetic Storage Devices, Xiaodong Li, Bharat Bhushan
Nanofatigue Studies Of Ultrathin Hard Carbon Overcoats Used In Magnetic Storage Devices, Xiaodong Li, Bharat Bhushan
Faculty Publications
A technique to perform nanofatigue experiments was developed. This technique utilizes a depth-sensing nanoindenter with harmonic force. The nanofatigue behavior of 20 nm thick amorphous carbon coatings was studied. The contact stiffness was monitored continuously throughout the test. The abrupt decrease in the contact stiffness indicates fatigue damage has occurred. The critical load amplitude, below which no fatigue damage occurs, was identified. It was found that the filtered cathodic arc coating exhibits longer fatigue life than a direct ion beam coating. Failure mechanisms of the coatings during fatigue are also discussed in conjunction with the hardness,elastic modulus, and fracture toughness, …
Bistable Operation Of A Two-Section 1.3-Mm Inas Quantum Dot Laser—Absorption Saturation And The Quantum Confined Stark Effect, Xiaodong Huang, A. Stintz, Hua Li, Audra Rice, G. T. Liu, L.F. Lester, Julian Cheng, K.J. Malloy
Bistable Operation Of A Two-Section 1.3-Mm Inas Quantum Dot Laser—Absorption Saturation And The Quantum Confined Stark Effect, Xiaodong Huang, A. Stintz, Hua Li, Audra Rice, G. T. Liu, L.F. Lester, Julian Cheng, K.J. Malloy
Faculty Publications
Room temperature, continuous-wave bistability was observed in oxide-confined, two-section, 1.3- m quantum-dot (QD) lasers with an integrated intracavity quantum-dot saturable absorber. The origin of the hysteresis and bistability were shown to be due to the nonlinear saturation of the QD absorption and the electroabsorption induced by the quantum confined Stark effect.