The Analysis Of The Tribological Properties Of Multiple Strengthened Nanocomposite Of The Cu-Al2o3 System, Zeljko J. Kamberovic

Zeljko J Kamberovic

This paper presents the results of examined tribological properties of the multiple strengthened nanocomposite Cu-Al2O3 system. Cu-Al2O3 composite powder was obtained by combination of the thermo-chemical procedure and mechanical alloying, which is a completely new approach to synthesis of these materials. The synthesized powders were cold pressed with 940MPa and sintered in hydrogen atmosphere in temperature range of 725-925o C during 15-120 minutes. The samples were thermo- mechanically treated in two stages after sintering: cold rolling with the final reduction degree of 30% and annealing at 800o C for 1h in hydrogen atmosphere. Characterization of the sintered, rolled and annealed …