Full-Text Articles in Engineering Science and Materials
The Effect Of Elevated Temperature On The Fretting Fatigue Behavior Of Nickel Alloy In-100, John F. Ownby
The Effect Of Elevated Temperature On The Fretting Fatigue Behavior Of Nickel Alloy In-100, John F. Ownby
Theses and Dissertations
This thesis studied the effect of elevated temperature (600 C) on the fretting fatigue behavior of IN-100. First, fretting and plain fatigue S-N curves were determined over a large range of applied stress at an identical stress ratio of 0.03 at 600 C and for fretting tests, with a constant contact load. The partial slip condition was verified by using hysteresis between shear force and axial stress techniques. The contact width and the crack initiation location were observed for all of the fretting specimens. The contact widths were consistent with expected values and the crack initiation location was at the …
Effects Of Polishing Shot-Peened Surfaces On Fretting Fatigue Behavior Of Ti-6al-4v, Kasey S. Scheel
Effects Of Polishing Shot-Peened Surfaces On Fretting Fatigue Behavior Of Ti-6al-4v, Kasey S. Scheel
Theses and Dissertations
The research of this thesis was done to investigate the effects of polishing a shot-peened specimen of Ti-6Al-4V on the fretting fatigue life of that specimen. The shot-peening process, though one of the most beneficial techniques in prolonging fretting fatigue life, creates a textured surface that may lead to problems on the micro level. This research was done in an attempt to further improve the peening process by examining the effects of another surface treatment to be used in conjunction, surface polishing. The rough peened surface may contain abrupt changes in surface geometry that act as stress risers, which are …
Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle
Tensile Stress Rupture Behavior Of A Woven Ceramic Matrix Composite In Humid Environments At Intermediate Temperature, Kevin J. Larochelle
Theses and Dissertations
Stress rupture tests on the SylramicTM fiber with an in-situ layer of boron nitride, boron nitride interphase, and SiC matrix ceramic matrix composite were performed at 550°C and 750°C with 0.0, 0.2, or 0.6 atm partial pressure of water vapor, pH2O. The 550°C, 100-hr strengths were 75%, 65% and 51% of the monotonic room temperature tensile strength, respectively. At 750°C, the strengths were 67%, 51%, and 49%, respectively. Field Emission Scanning Electron Microscopy analysis estimated the total embrittlement times for 550°C with 0.0, 0.2, and 0.6 atm pH2O were >63 hrs, >38 hrs, and between …
Role Of Plasticity On Fretting Fatigue Behavior Of Ti-6al-4v, Kisu Shin
Role Of Plasticity On Fretting Fatigue Behavior Of Ti-6al-4v, Kisu Shin
Theses and Dissertations
Fretting fatigue generally leads to the degradation of the fatigue strength of a material due to cyclic micro-slip between two contacting materials. Fretting fatigue is regarded as an important issue in designing aerospace structures. While many studies have evaluated fretting fatigue behavior under elastic deformation conditions, few studies have focused on fretting fatigue behavior under elastic-plastic deformation conditions. The primary goal of this study was to characterize the fretting fatigue crack initiation behavior in the presence of plasticity. Experimental tests were performed using pad configurations involving elastic-plastic deformations. In order to calculate stress distributions under elastic-plastic fretting fatigue conditions, FEA …
Effect Of A Variable Contact Load On Fretting Fatigue Behavior Of Ti-6al-4v, Andrew J. Jutte
Effect Of A Variable Contact Load On Fretting Fatigue Behavior Of Ti-6al-4v, Andrew J. Jutte
Theses and Dissertations
Effects of a variable contact load on the high cycle fretting fatigue behavior of Ti-6AL-4V were investigated. Experimental tests were performed using a new test setup capable of applying a contact load varying in amplitude, frequency, and phase and independently measuring shear forces on opposite sides of a specimen. Finite element analysis (FEA) of experimental and idealized loading conditions was performed and local mechanistic parameters and the Modified Shear Stress Range (MSSR) fatigue parameter were determined. Correlations between contact width, slip amplitude, fatigue life and a variable contact load were established with variable contact loading shown to have a damaging …
An Electromagnetic Tool For Damping And Fatigue Analysis, Todd M. Hoover
An Electromagnetic Tool For Damping And Fatigue Analysis, Todd M. Hoover
Theses and Dissertations
An automated test system was developed by the USAF Turbine Engine Fatigue Facility (TEFF). This system was initially designed to reduce the time and manpower required to characterize damping treatments. It is based on a digitally controlled environmental chamber with automated data acquisition and processing. Several outputs are available including identification of natural frequencies, modal damping ratios from the acquired frequency responses, and changes in damping with response amplitude; however, the TEFF additionally desires the capability to study fatigue under a free boundary condition. The system consists of a test specimen suspended by a pendulum to closely simulate free boundary …