Full-Text Articles in Biomedical Engineering and Bioengineering
Development Of Starch-Polyvinyl Alcohol (Pva) Biodegradable Film: Effect Of Cross-Linking Agent And Antimicrobials On Film Characteristics, Aniket Satish More, Chandani Sen, Madhusweta Das
Development Of Starch-Polyvinyl Alcohol (Pva) Biodegradable Film: Effect Of Cross-Linking Agent And Antimicrobials On Film Characteristics, Aniket Satish More, Chandani Sen, Madhusweta Das
Journal of Applied Packaging Research
To satisfy the need of developing eco-friendly flexible antimicrobial packaging film with minimum use of synthetic chemical ingredients, the present study examined the efficacy of citric acid (CA) as cross-linking agent and essential oils (EOs), viz., cinnamon essential oil (CEO) and oregano essential oil (OEO) as natural antimicrobials in corn starch-polyvinyl alcohol (CS-PVA) film. Compared to film prepared from filmogenic solution (FS) containing 75 kg CS+8.75 kg PVA+24.6 kg glycerol per m3 FS, film additionally containing CA at 0.07 kg/kg CS indicated 95% higher ultimate tensile strength (UTS) and 27% lower water vapor permeability (WVP). Film developed with incorporation …
Effect Of Plasticizer On Oxygen Permeability Of Cast Polylactic Acid (Pla) Films Determined Using Dynamic Accumulation Method, Kurniawan Yuniarto, Bruce A. Welt, Aris Purwanto, Hadi Karia Purwadaria, Ayman Abdellatief, Titi C. Sunarti, Setyo Purwanto
Effect Of Plasticizer On Oxygen Permeability Of Cast Polylactic Acid (Pla) Films Determined Using Dynamic Accumulation Method, Kurniawan Yuniarto, Bruce A. Welt, Aris Purwanto, Hadi Karia Purwadaria, Ayman Abdellatief, Titi C. Sunarti, Setyo Purwanto
Journal of Applied Packaging Research
Polylactic acid (PLA) is becoming an increasingly important biopolymer for packaging applications. PLA brittleness limits its applicability. This study evaluated PLA properties with increasing amounts of added polyethylene glycol (PEG) plasticizer. Oxygen transmission rate (OTR) of cast films was determined using the newly available Dynamic Accumulation (DA) method. Arrhenius temperature sensitivity of OTR and polymer Permeability was also determined. Permeability of neat PLA is 4.848 ml mm (STP)/m2 s kPa; hence, 4.84 ml mm (STP)/m2 s kPa, 4.07 ml mm (STP)/m2 s kPa and 5.42 ml mm (STP)/m2 s kPa by adding PEG 1 %, 5% …