Characterization Of Simulated Low Earth Orbit Space Environment Effects On Acid-Spun Carbon Nanotube Yarns, Ryan A. Kemnitz, Gregory R. Cobb, Abhendra K. Singh, Carl R. Hartsfield
Characterization Of Simulated Low Earth Orbit Space Environment Effects On Acid-Spun Carbon Nanotube Yarns, Ryan A. Kemnitz, Gregory R. Cobb, Abhendra K. Singh, Carl R. Hartsfield
Faculty Publications
The purpose of this study is to quantify the detrimental effects of atomic oxygen and ultraviolet (UV) C radiation on the mechanical properties, electrical conductivity, and piezoresistive effect of acid-spun carbon nanotube (CNT) yarns. Monotonic tensile tests with in-situ electrical resistance measurements were performed on pristine and exposed yarns to determine the effects of the atomic oxygen and UVC exposures on the yarn’s material properties. Both type of exposures were performed under vacuum to simulate space environment conditions. The CNT yarns’ mechanical properties did not change significantly after being exposed to UV radiation, but were significantly degraded by the atomic …
Mechanical Characterizations Of 3d-Printed Plla/Steel Particle Composites, Hozhabr Mozafari, Pengfei Dong, Haitham Hadidi, Michael P. Sealy, Linxia Gu
Mechanical Characterizations Of 3d-Printed Plla/Steel Particle Composites, Hozhabr Mozafari, Pengfei Dong, Haitham Hadidi, Michael P. Sealy, Linxia Gu
Department of Mechanical and Materials Engineering: Faculty Publications
The objective of this study is to characterize the micromechanical properties of poly-L-lactic acid (PLLA) composites reinforced by grade 420 stainless steel (SS) particles with a specific focus on the interphase properties. The specimens were manufactured using 3D printing techniques due to its many benefits, including high accuracy, cost effectiveness and customized geometry. The adopted fused filament fabrication resulted in a thin interphase layer with an average thickness of 3 μm. The mechanical properties of each phase, as well as the interphase, were characterized by nanoindentation tests. The effect of matrix degradation, i.e., imperfect bonding, on the elastic modulus of …