Nanoindentation Characterization On Local Plastic Response Of Ti-6al-4v Under High-Load Spherical Indentation, Yan Wen, Lechun Xie, Zhou Wang, Liqiang Wang, Weijie Lu, Laichang Zhang Jan 2019

Nanoindentation Characterization On Local Plastic Response Of Ti-6al-4v Under High-Load Spherical Indentation, Yan Wen, Lechun Xie, Zhou Wang, Liqiang Wang, Weijie Lu, Laichang Zhang

ECU Publications Post 2013

After high-load spherical indentation treatment, the variations of hardness on the plastic zone of Ti-6Al-4V were investigated via nanoindentation method. The hardness within the center of plastic zone was measured by nanoindenter, and the magnitude decreased gradually along the depth, which were caused by the different extent of plastic deformation under the residual imprint. The microstructure of indentation were observed using scanning electron microscope (SEM) before and after surface etching, and the results showed that the microhardness revealed the average hardness of α and β phases of Ti-6Al-4V. The maximum hardness reached 6.438 GPa in the depth of 132 ...


Beta-Type Ti-Nb-Zr-Cr Alloys With Large Plasticity And Significant Strain Hardening, Syed F. Jawed, Chirag D. Rabadia, Y. J. Liu, L. Q. Wang, Y. H. Li, X. H. Zang, Laichang C. Zhang Jan 2019

Beta-Type Ti-Nb-Zr-Cr Alloys With Large Plasticity And Significant Strain Hardening, Syed F. Jawed, Chirag D. Rabadia, Y. J. Liu, L. Q. Wang, Y. H. Li, X. H. Zang, Laichang C. Zhang

ECU Publications Post 2013

A series of Ti-25Nb-8Zr-xCr (x = 0, 2, 4, 6, 8 wt%) alloys were designed based on DV-Xα cluster method and e=a-Δr diagram with an anticipation to obtain high plasticity and significant strain hardening. The designed alloys were produced through cold crucible levitation melting technique in order to effectively investigate their micro-structures and mechanical properties. The addition of Cr significantly enhances the β stability in the microstructures of the Ti-25Nb-8Zr-xCr alloys. Both yield strength and hardness of the studied alloys increase due to the effect of solid-solution strengthening. By contrast, the plasticity, maximum strength and strain hardening rate are influenced ...