Effect Of Interfacial Mobility On Flexural Strength And Fracture Toughness Of Glass/Epoxy Laminates, T. W. H. Wang, Frank D. Blum, Lokeswarappa R. Dharani

Chemistry Faculty Research & Creative Works

Mechanical testing and surface fractography were used to characterize the fracture of E-glass fiber reinforced epoxy composites as a function of the silane coupling agent used. gamma-Aminopropyltriethoxysilane (APS) and delta-aminobutyltriethoxysilane (ABS) were used because these have been shown to have different interfacial mobilities at multilayer coverage. The values of the properties studied generally increased from untreated c, as determined from a Mode I translaminar fracture toughness tests, for the untreated composites (10.5 ± 0.4 kJ/m2) was lower than that for the ABS-treated composites (14.3 ± 2.1 kJ/m2) which was lower than that for the APS-treated composites (17.1 ± 2.4 kJ/m2). …