Microstructure And Interface Characteristics Of B4c, Sic And Al2o3 Reinforced Al Matrix Composites: A Comparative Study
A.S. Md Abdul Haseeb
Three aluminium metal matrix composites containing reinforcing particles of B4C, SiC and Al2O3 (0-20vol.%) were processed. The stir-casting manufacturing route followed by hot extrusion was utilized, being one of the cost-effective industrial methods. A clear interfacial reaction product/layer was found at Al-SiC interface for composites held for a relatively long processing time (>30 min). No reaction product was observed at Al-B4C and Al-Al2O3 interfaces at the resolution limit of the SEM used. On the other hand, two secondary phases (alumina and another phase containing aluminium, boron and carbon) were found in the aluminum matrix away from the interface in …
Microstructure And Interface Characteristics Of B4c, Sic And Al2o3 Reinforced Al Matrix Composites: A Comparative Study
A.S. Md Abdul Haseeb
Three aluminium metal matrix composites containing reinforcing particles of B4C, SiC and Al2O3 (0-20vol.%) were processed. The stir-casting manufacturing route followed by hot extrusion was utilized, being one of the cost-effective industrial methods. A clear interfacial reaction product/layer was found at Al-SiC interface for composites held for a relatively long processing time (>30 min). No reaction product was observed at Al-B4C and Al-Al2O3 interfaces at the resolution limit of the SEM used. On the other hand, two secondary phases (alumina and another phase containing aluminium, boron and carbon) were found in the aluminum matrix away from the interface in …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …
Wear Failure Of A Leaded Bronze Bearing: Correlation Between Plant Experience And Laboratory Wear Test Data
A.S. Md Abdul Haseeb
This paper describes an investigation on the failure of a large leaded bronze bearing that supports a nine-ton roller of a plastic calendering machine. At the end of the normal service life of a good bearing, which lasted for seven years, a new bearing was installed. However the new one failed catastrophically within a few days, generating a huge amount of metallic wear debris and causing pitting on the surface of the cast iron roller. Following the failure, samples were collected from both good and failed bearings. The samples were analyzed chemically and their microstructures examined. Both samples were subjected …