Manipulating Coupling State And Magnetism Of Mn-Doped Zno Nanocrystals By Changing The Coordination Environment Of Mn Via Hydrogen Annealing, Yan Cheng, W Li, Weichang Hao, Huaizhe Xu, Zhongfei Xu, Li Rong Zheng, Jing Zhang, S X. Dou, Tianmin Wang
Manipulating Coupling State And Magnetism Of Mn-Doped Zno Nanocrystals By Changing The Coordination Environment Of Mn Via Hydrogen Annealing, Yan Cheng, W Li, Weichang Hao, Huaizhe Xu, Zhongfei Xu, Li Rong Zheng, Jing Zhang, S X. Dou, Tianmin Wang
Australian Institute for Innovative Materials - Papers
Mn-doped ZnO nanocrystals are synthesized by a wet chemical route and treated in H2/Ar atmosphere with different H2/Ar ratios. It is found that hydrogen annealing could change the coordination environment of Mn in ZnO lattice and manipulate the magnetic properties of Mn-doped ZnO. Mn ions initially enter into interstitial sites and a Mn3+O6 octahedral coordination is produced in the prepared Mn-doped ZnO sample, in which the nearest neighbor Mn3+ and O2 ions could form a Mn3+-O2--Mn3+ complex. After H2 annealing, interstitial Mn ions can substitute for Zn to generate the Mn2+O4 tetrahedral coordination in the nanocrystals, in which neighboring Mn2+ …
Interface-Enhanced Electron-Phonon Coupling And High-Temperature Superconductivity In Potassium-Coated Ultrathin Fese Films On Srtio3, Chenjia Tang, Chong Liu, Guanyu Zhou, Fangsen Li, Hao Ding, Zhi Li, Ding Zhang, Zheng Li, Canli Song, Shuaihua Ji, Ke He, Lili Wang, Xucan Ma, Qi-Kun Xue
Interface-Enhanced Electron-Phonon Coupling And High-Temperature Superconductivity In Potassium-Coated Ultrathin Fese Films On Srtio3, Chenjia Tang, Chong Liu, Guanyu Zhou, Fangsen Li, Hao Ding, Zhi Li, Ding Zhang, Zheng Li, Canli Song, Shuaihua Ji, Ke He, Lili Wang, Xucan Ma, Qi-Kun Xue
Australian Institute for Innovative Materials - Papers
Alkali-metal (potassium) adsorption on FeSe thin films with thickness from 2 unit cells (UC) to 4 UC on SrTiO3 grown by molecular beam epitaxy is investigated with a low-temperature scanning tunneling microscope. At appropriate potassium coverage (0.20-0.25 monolayer), the tunneling spectra of the films all exhibit a superconductinglike gap which is overall larger than 11 meV (five times the gap value of bulk FeSe) and decreases with increasing thickness, and two distinct features of characteristic phonon modes at ∼11 and ∼21 meV. The results reveal the critical role of the interface-enhanced electron-phonon coupling for possible high-temperature superconductivity in ultrathin FeSe …