Influence Of Coating Defects Within The Lock Seams On The Corrosion Performance Of Aluminized Steel Drainage Pipes, Mohammed Al Yaarubi
Influence Of Coating Defects Within The Lock Seams On The Corrosion Performance Of Aluminized Steel Drainage Pipes, Mohammed Al Yaarubi
USF Tampa Graduate Theses and Dissertations
The electrochemical behavior of aluminized steel is investigated to determine the corrosion performance of coating deficiencies generated within the lock seams during the fabrication of aluminized steel corrugated pipe. Electrochemical techniques and visual and profilometric analysis are used to assess the ability of the aluminum and zinc coating to provide sufficient galvanic protection to the underlying steel in the presence of a crevice. Also, Crevice coupons and lock-seam samples were used in this investigation in different environmental conditions simulating natural water conditions to relate the corrosion rate with the level of protection that the coating will provide. In addition, a …
Effects Of Physical And Chemical Characteristics Of Slags And Cements On Durability Of Portland Cement-Slag Blended Systems, Farzaneh Nosouhian
Effects Of Physical And Chemical Characteristics Of Slags And Cements On Durability Of Portland Cement-Slag Blended Systems, Farzaneh Nosouhian
USF Tampa Graduate Theses and Dissertations
Ground granulated blast furnace slag (GGBFS) which is a commonly used supplementary cementitious material (SCM) needs to be more investigated for improving durability of concrete elements and service life of concrete structures. This research focuses on the effect of the physical and chemical characteristics of GGBFS and portland cement on durability of portland cement-slag blended systems. The effect of cement replacement level is also investigated using control mixes (no slag) and four different levels of slag content. To this end, eight GGBFS and eight portland cements were selected based on their physical characteristics and chemical composition. Four series of experimental …
Corrosion Of Steel In Submerged Concrete Structures, Michael Thomas Walsh
Corrosion Of Steel In Submerged Concrete Structures, Michael Thomas Walsh
USF Tampa Graduate Theses and Dissertations
This investigation determined that severe corrosion of steel can occur in the submerged portions of reinforced concrete structures in marine environments. Field studies of decommissioned pilings from actual bridges revealed multiple instances of strong corrosion localization, showing appreciable local loss of steel cross-section. Quantitative understanding of the phenomenon and its causes was developed and articulated in the form of a predictive model. The predictive model output was consistent with both the corrosion rate estimates and the extent of corrosion localization observed in the field observations. The most likely explanation for the observed phenomena that emerged from the understanding and modeling …