Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel is currently in regular use as an alternative fuel over conventional petroleum diesel. However, corrosion of automotive materials is one of the concerns related to biodiesel compatibility issues. In addition, auto-oxidation of biodiesel can also enhance the corrosiveness of biodiesel. The present study aims to investigate inhibition effect of ethylenediamine (EDA), n-butylamine (nBA), tert-butylamine (TBA) against corrosion of cast iron. Static immersion tests in biodiesel in the presence (100 ppm) and absence of different corrosion inhibitors were carried out at room temperature for 1200 hours. At the end of the test, corrosion characteristic was investigated by weight loss measurements …
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
Effect Of Different Corrosion Inhibitors On The Corrosion Of Cast Iron In Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel is currently in regular use as an alternative fuel over conventional petroleum diesel. However, corrosion of automotive materials is one of the concerns related to biodiesel compatibility issues. In addition, auto-oxidation of biodiesel can also enhance the corrosiveness of biodiesel. The present study aims to investigate inhibition effect of ethylenediamine (EDA), n-butylamine (nBA), tert-butylamine (TBA) against corrosion of cast iron. Static immersion tests in biodiesel in the presence (100 ppm) and absence of different corrosion inhibitors were carried out at room temperature for 1200 hours. At the end of the test, corrosion characteristic was investigated by weight loss measurements …
Effect Of Temperature On The Corrosion Behavior Of Mild Steel Upon Exposure To Palm Biodiesel
Effect Of Temperature On The Corrosion Behavior Of Mild Steel Upon Exposure To Palm Biodiesel
A.S. Md Abdul Haseeb
Recently biodiesel, as an alternative fuel is getting more significance to replace diesel fuel completely or partially. However, corrosion of automotive materials in biodiesel is a major concern as this can reduce engine life. This study aims to investigate the corrosion behavior of mild steel at three different temperatures such as room temperature, 50 and 80 °C. Static immersion tests in B0 (diesel), B50 (50% biodiesel in diesel), B100 (biodiesel) were carried out for 1200 h. At the end of the tests, corrosion characteristic was investigated by weight loss measurements and changes of the exposed metal surface. Fuels were analyzed …