Influence Of Ni Nanoparticle On The Morphology And Growth Of Interfacial Intermetallic Compounds Between Sn-3.8ag-0.7cu Lead-Free Solder And Copper Substrate
A.S. Md Abdul Haseeb
This paper reports on the effects of adding Ni nanoparticles to a Sn-3.8Ag-0.7Cu solder. The nanocomposite was prepared by manual blending of SAC solder paste with various percentages of Ni particles. Results showed that the addition of Ni nanoparticles did not bring any significant change in the onset melting temperature of the solder. An increase in the weight percentage of nanoparticles in the solder caused an increase of the wetting angle and a decrease of spreading rate. Moreover, the addition of Ni nanoparticles changed the interfacial intermetallic compound morphology from a scalloped structure into a planar type structure, enhanced the …
Effects Of Reflow On The Interfacial Characteristics Between Zn Nanoparticles Containing Sn-3.8ag-0.7cu Solder And Copper Substrate
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to investigate the effects of zinc (Zn) nanoparticles on the interfacial intermetallic compounds (IMCs) between Sn-3.8Ag-0.7Cu (SAC) solder and Cu substrate during multiple reflow. Design/methodology/approach - The nanocomposite solders were prepared by manually mixing of SAC solder paste with varying amounts of Zn nanoparticles. The solder pastes were reflowed on a hotplate at 250 C for 45 s for up to six times. The actual Zn content after reflow was analyzed by inductively coupled plasma-optical emission spectroscopy (ICP-OES). The wetting behavior of the solders was characterized by analyzing the contact angles and …
Effects Of Reflow On The Interfacial Characteristics Between Zn Nanoparticles Containing Sn-3.8ag-0.7cu Solder And Copper Substrate
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to investigate the effects of zinc (Zn) nanoparticles on the interfacial intermetallic compounds (IMCs) between Sn-3.8Ag-0.7Cu (SAC) solder and Cu substrate during multiple reflow. Design/methodology/approach - The nanocomposite solders were prepared by manually mixing of SAC solder paste with varying amounts of Zn nanoparticles. The solder pastes were reflowed on a hotplate at 250 C for 45 s for up to six times. The actual Zn content after reflow was analyzed by inductively coupled plasma-optical emission spectroscopy (ICP-OES). The wetting behavior of the solders was characterized by analyzing the contact angles and …
Effects Of Reflow On The Interfacial Characteristics Between Zn Nanoparticles Containing Sn-3.8ag-0.7cu Solder And Copper Substrate
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to investigate the effects of zinc (Zn) nanoparticles on the interfacial intermetallic compounds (IMCs) between Sn-3.8Ag-0.7Cu (SAC) solder and Cu substrate during multiple reflow. Design/methodology/approach - The nanocomposite solders were prepared by manually mixing of SAC solder paste with varying amounts of Zn nanoparticles. The solder pastes were reflowed on a hotplate at 250 C for 45 s for up to six times. The actual Zn content after reflow was analyzed by inductively coupled plasma-optical emission spectroscopy (ICP-OES). The wetting behavior of the solders was characterized by analyzing the contact angles and …
Electrodeposition Of Lead-Free Solder Alloys
Electrodeposition Of Lead-Free Solder Alloys
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to enhance the understanding on the electrodeposition of various lead (Pb)-free solder alloys, so that new studies can be carried out to solve processing issues. Design/methodology/approach - The paper reviews the available reports on the electrodeposition of tin (Sn)-based solder systems and identifies the challenges in this area. Findings - Compositional control remains a major challenge in this area, where the achievement of desired composition for binary and ternary alloys is subjected to uncertainties. The use of chelating agents in the bath and optimization of parameters can assist the achievement of near-desired …
Stability Of Molybdenum Nanoparticles In Sn-3.8ag-0.7cu Solder During Multiple Reflow And Their Influence On Interfacial Intermetallic Compounds
A.S. Md Abdul Haseeb
This work investigates the effects of molybdenum nanoparticles on the growth of interfacial intermetallic compound between Sn-3.8Ag-0.7Cu solder and copper substrate during multiple reflow. Molybdenum nanoparticles were mixed with Sn-3.8Ag-0.7Cu solder paste by manual mixing. Solder samples were reflowed on a copper substrate in a 250 °C reflow oven up to six times. The molybdenum content of the bulk solder was determined by inductive coupled plasma-optical emission spectrometry. It is found that upon the addition of molybdenum nanoparticles to Sn-3.8Ag-0.7Cu solder, the interfacial intermetallic compound thickness and scallop diameter decreases under all reflow conditions. Molybdenum nanoparticles do not appear to …
Die Attach Properties Of Zn-Al-Mg-Ga Based High-Temperature Lead-Free Solder On Cu Lead-Frame
Die Attach Properties Of Zn-Al-Mg-Ga Based High-Temperature Lead-Free Solder On Cu Lead-Frame
A.S. Md Abdul Haseeb
No abstract provided.
Addition Of Cobalt Nanoparticles Into Sn-3.8ag-0.7cu Lead-Free Solder By Paste Mixing
Addition Of Cobalt Nanoparticles Into Sn-3.8ag-0.7cu Lead-Free Solder By Paste Mixing
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to investigate the effects of addition Co nanoparticles on the characteristic properties of Sn-3.8Ag-0.7Cu solder. Design/methodology/approach - Cobalt (Co) nanoparticles were added to Sn-Ag-Cu solders by thoroughly blending various weight percentages (0-2.0 wt%) of Co nanoparticles with near eutectic SAC387 solder paste. Blending was done mechanically for 30 min to ensure a homogeneous mixture. The paste mixture was then reflowed on a hot plate at 250°C for 45 s. The melting points of nanocomposite solder were determined by differential scanning calorimetry. Spreading rate of nanocomposite was calculated following the JIS Z3198-3 standard. …
Interfacial Reaction And Dissolution Behavior Of Cu Substrate In Molten Sn-3.8ag-0.7cu In The Presence Of Mo Nanoparticles
A.S. Md Abdul Haseeb
Purpose - In electronic packaging, when solid copper comes in contact with liquid solder alloy, the former dissolves and intermetallic compounds (IMCs) form at the solid-liquid interface. The purpose of this paper is to study the effect of the presence of molybdenum nanoparticles on the dissolution of copper and the formation of interfacial IMC. Design/methodology/approach - Cu wire having a diameter of 250 μm is immersed in liquid composite solders at 250° up to 15 min. Composite solder was prepared by adding various amount of Mo nanoparticles into the Sn-3.8Ag-0.7Cu (SAC) solder paste. The dissolution behavior of Cu substrate is …
Understanding The Effects Of Addition Of Copper Nanoparticles To Sn-3.5 Ag Solder
Understanding The Effects Of Addition Of Copper Nanoparticles To Sn-3.5 Ag Solder
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to focus on the fabrication of SAC nanocomposites solder and discuss the effects of nanoCu addition on the structure and properties of resulted nanocomposite solder. Design/methodology/ approach - Ball milling is a nonequilibrium processing technique for producing composite metal particles with submicron homogeneity by the repeated cold welding and fracture of powder particles. This method is believed to offer good processablity, precise control over the solder composition, and produce more homogeneous mixture. Findings - It is found that the melting temperature, the wetting behaviour, and hardness are improved when the Cu nanoparticles …