Preparation And Low-Temperature Sintering Of Cu Nanoparticles For High-Power Devices
Preparation And Low-Temperature Sintering Of Cu Nanoparticles For High-Power Devices
A.S. Md Abdul Haseeb
One of the fundamental requirements for high-temperature electronic packaging is reliable silicon attach with low and stable electrical resistance. This paper presents a study conducted on Cu nanoparticles as an alternative lead-free interconnect material for high-temperature applications. Cu nanoparticles were prepared using pulsed wire evaporation technique in water medium. Pure Cu nanoparticles without any organic mixture were used in this paper. An economical approach to extract the nanoparticles from water was established. In situ Cu nanoparticles oxide reduction was successfully done using forming gas $({\rm N}-{2}{\hbox{-}}5\%{\rm H}-{2})$. Cross-section analysis on bonded interface shows onset of Cu nanoparticles sintering at 400$^{\circ}{\rm …
Stability Of Molybdenum Nanoparticles In Sn-3.8ag-0.7cu Solder During Multiple Reflow And Their Influence On Interfacial Intermetallic Compounds
A.S. Md Abdul Haseeb
This work investigates the effects of molybdenum nanoparticles on the growth of interfacial intermetallic compound between Sn-3.8Ag-0.7Cu solder and copper substrate during multiple reflow. Molybdenum nanoparticles were mixed with Sn-3.8Ag-0.7Cu solder paste by manual mixing. Solder samples were reflowed on a copper substrate in a 250 °C reflow oven up to six times. The molybdenum content of the bulk solder was determined by inductive coupled plasma-optical emission spectrometry. It is found that upon the addition of molybdenum nanoparticles to Sn-3.8Ag-0.7Cu solder, the interfacial intermetallic compound thickness and scallop diameter decreases under all reflow conditions. Molybdenum nanoparticles do not appear to …