Fatigue Behavior Of An Advanced Sic/Sic Composite With An Oxidation Inhibited Matrix At 1200°C In Air And In Steam, Jacob Delapasse
Fatigue Behavior Of An Advanced Sic/Sic Composite With An Oxidation Inhibited Matrix At 1200°C In Air And In Steam, Jacob Delapasse
Theses and Dissertations
The fatigue behavior of an advanced Silicon Carbide/Silicon Carbide (SiC/SiC) ceramic matrix composite (CMC) with oxidation inhibited matrix was investigated at 1200˚C in laboratory air and in steam environments. The composite consisted of an oxidation inhibited SiC matrix reinforced with Hi-Nicalon fibers coated with pyrolytic carbon (PyC) with a boron carbide overlay woven into eight-harness-satin (8HS) weave plies. Tensile stress-strain behavior and tensile properties were evaluated at 1200˚C. Tension-tension fatigue tests were conducted in both laboratory air and in steam at 1200˚C at frequencies of 0.1 Hz, 1.0 Hz, and 10 Hz. The tension-tension fatigue tests had a ratio of …
Modeling Of Progressive Damage In Fiber-Reinforced Ceramic Matrix Composites, James P. Solti
Modeling Of Progressive Damage In Fiber-Reinforced Ceramic Matrix Composites, James P. Solti
Theses and Dissertations
An analytic methodology is developed to model the response of fiber-reinforced ceramic matrix composites (CMOs) when subjected to monotonic and fatigue loadings. The analysis requires the formulation of (1) a micromechanics model which defines the laminate's geometry and constitutive relationship; (2) failure criteria which estimate the extent of microstructural damage, and, finally, (3) a means of analyzing frictional slip, fiber pull-out, interfacial wear and laminate failure. For the present study, the behavior of unidirectional and crossply CMOs is investigated using modified shear-lag theory in conjunction with a set of failure criteria with a minimum reliance on empirical data. The damage …
Thermo-Mechanical Fatigue Behavior Of Cross-Ply Ceramic Matrix Composite Under Tension-Tension Loading, Dana G. Allen
Thermo-Mechanical Fatigue Behavior Of Cross-Ply Ceramic Matrix Composite Under Tension-Tension Loading, Dana G. Allen
Theses and Dissertations
The purpose of this study was to investigate the combined effect of cyclic temperature and loading on the fatigue life of a ceramic matrix composite with a cross ply lay-up. The material used in this study was a potassium borosilicate glass (BSG) doped magnesium aluminosilicate (MAS) cordierite matrix reinforced with Nicalon (silicon carbide, SiC) fibers in a [0/90]4s lay-up. Thermomechanical fatigue (TMF) tests were performed with a period of 180 seconds/cycle, or 0.00556 Hz, and a triangular wave-form. The temperature was cycled between 566°C and l093°C, and the stress levels varied between 60 MPa and 145 MPa. All tests …