Synthesis And Optimization Of Fluorine-Free Y And Cu Precursor Solution For Mod Processing Of Ybco Coated Conductor, Jaimoo Yoo, Young-Kuk Kim, Kookchae Chung, Jaewoong Ko, Xiaolin Wang, S X. Dou
Synthesis And Optimization Of Fluorine-Free Y And Cu Precursor Solution For Mod Processing Of Ybco Coated Conductor, Jaimoo Yoo, Young-Kuk Kim, Kookchae Chung, Jaewoong Ko, Xiaolin Wang, S X. Dou
Shi Xue Dou
MOD solutions for YBCO coated conductors were synthesized with fluorine-free Y & Cu precursor. The fluorine content in the precursor solution was significantly reduced and a fast calcination profile was realized. A crack-free & thick precursor film was successfully obtained just after less than 2 hours of calcination in wet O2 atmosphere. Optimization of the precursor solution with Sm addition enables further improvement of thickness and uniformity of precursor films. The calcinated precursor film was successfully converted to dense and uniform YBCO film after annealing in wet Ar/O2 atmosphere. The measured critical current value was about 273 A/cm-w (Jc ~ …
A Study On The Charge-Discharge Mechanism Of Co3o4 As An Anode For The Li Ion Secondary Battery, Yong-Mook Kang, Min-Sang Song, Jin-Ho Kim, Hyun-Seok Kim, Min-Sik Park, Jai-Young Lee, Hua-Kun Liu, S X. Dou
A Study On The Charge-Discharge Mechanism Of Co3o4 As An Anode For The Li Ion Secondary Battery, Yong-Mook Kang, Min-Sang Song, Jin-Ho Kim, Hyun-Seok Kim, Min-Sik Park, Jai-Young Lee, Hua-Kun Liu, S X. Dou
Shi Xue Dou
Co3O4 has shown acceptable electrochemical properties as the anode material of Li secondary batteries. In detail, its capacity reached about 700 mAh/g, twice as high as graphite, and 93.4% of initial capacity was retained after 100 cycles. EIS (electrochemical impedance spectroscopy) analyses revealed that after the 1st cycle, the insertion or extraction of Li ions in Co3O4 can occur homogeneously and reversibly (randless-like behavior, homogeneous mixture: Co + Li2O (in the state of Li insertion), Co3O4 (in the state of Li extraction)). In fact, the coulombic efficiency of Co3O4 was almost 100% except for the 1st cycle. According to P. …
Silicon Oil: A Cheap Liquid Additive For Enhancing In-Field Critical Current Density In Mgb2, Xiaolin Wang, Zhenxiang Cheng, S X. Dou
Silicon Oil: A Cheap Liquid Additive For Enhancing In-Field Critical Current Density In Mgb2, Xiaolin Wang, Zhenxiang Cheng, S X. Dou
Shi Xue Dou
In this work, the authors report on significant flux pinning enhancement in MgB2 that has been easily obtained using a liquid additive, silicon oil. MgB2 bulk samples with 0 up to 30 wt % silicon oil added were prepared by an in situ reaction. Results showed that the Si and C released from the decomposition of the silicon oil formed Mg2Si and substituted into B sites, respectively. Increasing the amount of the Si oil up to 15 wt % has resulted in the reduction of the lattice parameters, as well as Tc and R(300 K)/R(Tc) values, accompanied by a significant …
Flux-Pinning Mechanism In Silicone-Oil Doped Mgb2: Evidence For Charge-Carrier Mean Free Path Fluctuation Pinning, Shaban R. Ghorbani, Xiaolin Wang, S X. Dou, Sung-Ik Lee, Md S. Hossain
Flux-Pinning Mechanism In Silicone-Oil Doped Mgb2: Evidence For Charge-Carrier Mean Free Path Fluctuation Pinning, Shaban R. Ghorbani, Xiaolin Wang, S X. Dou, Sung-Ik Lee, Md S. Hossain
Shi Xue Dou
Flux-pinning mechanism of MgB2 doped with 10 wt % silicone-oil sintered at low and high temperatures has been investigated by magnetic measurements. The field dependence of the critical current density, jc(B), was analysed within the collective pinning model. A crossover field, Bsb, from the single vortex to the small vortex bundle-pinning regime was observed. For both types of sintered samples, the temperature dependence of Bsb(T) at low temperature is in good agreement with the δl pinning mechanism, i.e., pinning associated with charge-carrier mean free path fluctuation. At temperatures close to the critical temperature, however, there is evidence for δTc pinning, …