Characteristics Of The Hydrogen Electrode In High Temperature Steam Electrolysis Process, Chao Jin, Chenghao Yang, Fanglin Chen
Characteristics Of The Hydrogen Electrode In High Temperature Steam Electrolysis Process, Chao Jin, Chenghao Yang, Fanglin Chen
Faculty Publications
YSZ-electrolyte supported solid oxide electrolyzer cells (SOECs) using LSM-YSZ oxygen electrode but with three types of hydrogen electrode, Ni–SDC, Ni–YSZ and LSCM–YSZ have been fabricated and characterized under different steam contents in the feeding gas at 850°C. Electrochemical impedance spectra results show that cell resistances increase with the increase in steam concentrations under both open circuit voltage and electrolysis conditions, suggesting that electrolysis reaction becomes more difficult in high steam content. Pt reference electrode was applied to evaluate the contributions of the hydrogen electrode and oxygen electrode in the electrolysis process. Electrochemical impedance spectra and over potential of both electrodes …
Sr2Fe1.5Mo0.5O6 As Cathodes For Intermediate-Temperature Solid Oxide Fuel Cells With La0.8Sr0.2Ga0.87Mg0.13O3 Electrolyte, Guoliang Xiao, Qiang Liu, Fei Zhao, Lei Zhang, Changrong Xia, Fanglin Chen
Sr2Fe1.5Mo0.5O6 As Cathodes For Intermediate-Temperature Solid Oxide Fuel Cells With La0.8Sr0.2Ga0.87Mg0.13O3 Electrolyte, Guoliang Xiao, Qiang Liu, Fei Zhao, Lei Zhang, Changrong Xia, Fanglin Chen
Faculty Publications
The performance of Sr2Fe1.5Mo0.5O6 (SFMO) as a cathode material has been investigated in this study. The oxygen ionic conductivityof SFMO reaches 0.13 S cm-1 at 800°C in air. The chemical diffusion coefficient (Dchem) and surface exchange constant (kex) of SFMO at 750°C are 5.0 x 10-6 cm2 s-1 and 2.8 x 10-5 cm s-1, respectively, suggesting that SFMO may have good electrochemicalactivity for oxygen reduction. SFMO shows a thermal expansion coefficient (TEC) of 14.5 x 10-6 K-1 the …
La0.85Sr0.15Mno3− Infiltrated Y0.5Bi1.5O3 Cathodes For Intermediate-Temperature Solid Oxide Fuel Cells, Jiang Zhiyi, Changrong Xia, Fei Zhao, Fanglin Chen
La0.85Sr0.15Mno3− Infiltrated Y0.5Bi1.5O3 Cathodes For Intermediate-Temperature Solid Oxide Fuel Cells, Jiang Zhiyi, Changrong Xia, Fei Zhao, Fanglin Chen
Faculty Publications
Porous yttria-stabilized bismuth oxides (YSB) were investigated as the backbones for (LSM) infiltrated cathodes in intermediate-temperature solid oxide fuel cells. The cathodes were evaluated using anode-supported single cells with scandia-stabilized zirconia as the electrolytes. With humidified as the fuel, the cell showed peak power density of 0.33, 0.52, and at 650, 700, and , respectively. At , the cell polarization resistance was only , of the lowest value previously reported, indicating that YSB is a promising backbone for the LSM infiltrated cathode.
Increasing Power Density Of Lsgm-Based Solid Oxide Fuel Cells Using New Anode Materials, Kevin Huang, Jen-Hau Wan, John B. Goodenough
Increasing Power Density Of Lsgm-Based Solid Oxide Fuel Cells Using New Anode Materials, Kevin Huang, Jen-Hau Wan, John B. Goodenough
Faculty Publications
Chemical reactions between the superior perovskite oxide-ion conductor Sr- and Mg-doped LaGaO3 (LSGM), CeO2, and NiO have been studied by powder X-ray diffraction. The results showed that an extensive reactivity occurs as a result of La migration driven by a gradient of La chemical activity. La migration across the LSGM/electrode interfaces in a fuel cell leads to the formation of resistive phases at the interface, either LaSrGa3O7 or LaSrGaO4. Use of 40 mol % La2O3 -doped CeO2 as an interlayer between anode and electrolyte as well as in …
Oxygen Permeation Through Cobalt-Containing Perovskites: Surface Oxygen Exchange Vs. Lattice Oxygen Diffusion, Kevin Huang, John B. Goodenough
Oxygen Permeation Through Cobalt-Containing Perovskites: Surface Oxygen Exchange Vs. Lattice Oxygen Diffusion, Kevin Huang, John B. Goodenough
Faculty Publications
The oxygen permeation fluxes from p′O2 to pnO2 (p′O2>pnO2) across cobalt-containing perovskite ceramic membranes La1−xSrxCoO3−δ and SrCo0.8Fe0.2O3−δ were measured by gas chromatography as functions of oxygen chemical potential gradient, temperature, thickness, and catalytic activity on the surface. Power indexes 0.5>n>0 for uncatalyzed La1−xSrxCoO3−δ and 1>n>0.5 for SrCo0.8Fe0.2O3−δ were obtained when JO2 vs. p′nO2−p'′nO2 …
Electrode Performance Test On Single Ceramic Fuel Cells Using As Electrolyte Sr‐ And Mg‐Doped Lagao3, Kevin Huang, Man Feng, John B. Goodenough, Christopher Milliken
Electrode Performance Test On Single Ceramic Fuel Cells Using As Electrolyte Sr‐ And Mg‐Doped Lagao3, Kevin Huang, Man Feng, John B. Goodenough, Christopher Milliken
Faculty Publications
The electrode performance of a single solid oxide fuel cell was evaluated using a 500 μm thick La0.9Sr0.1Ga0.8Mg0.2O2.85 (LSGM) as the electrolyte membrane. Comparison of La0.6Sr0.4CoO3-δ (LSCo) and La0.9Sr0.1MnO3 (LSM) as cathodes showed LSCo gave an exchange current density two orders of magnitude higher than that of LSM. Comparison of CeO2/Ni and LSGM/Ni as anodes showed a degradation of the latter with time, and studies of the anode‐electrolyte interface and the reactivity of NiO and LSGM suggest better anode …