Corrosion Mechanism Of Copper In Palm Biodiesel
Corrosion Mechanism Of Copper In Palm Biodiesel
A.S. Md Abdul Haseeb
Biodiesel is a promising alternative fuel. However, it causes enhanced corrosion of automotive materials, especially of copper based components. In the present study, corrosion mechanism of copper was investigated by scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Compositional change of biodiesel due to the exposure of copper was also investigated. Corrosion patina on copper is found to be composed of Cu2O, CuO, Cu(OH)2 and CuCO3. Dissolved O2, H2O, CO2 and RCOO- radical in biodiesel seem to be the leading factors in enhancing the corrosiveness of biodiesel. © 2012 Elsevier Ltd.
The Wear Behavior Of Cross-Linked Uhmwpe Under Dry And Bovine Calf Serum-Lubricated Conditions
The Wear Behavior Of Cross-Linked Uhmwpe Under Dry And Bovine Calf Serum-Lubricated Conditions
A.S. Md Abdul Haseeb
The present study was performed to investigate the effects of gamma radiation on the wear behavior of unirradiated and irradiated ultra-high-molecular-weight polyethylene (UHMWPE) against Ti-6Al-4V under dry and lubricated conditions at different applied loads. The UHMWPE specimens were exposed directly to nominal doses of 0, 25, 40, 50, and 100 kGy. Scanning electron microscope (SEM) analysis of the worn surface of UHMWPE and Ti-6Al-4V was performed to understand the mechanism of wear involved between the contact surfaces during wear testing. From the wear test results, there were significant differences between the wear of unirradiated UHMWPE and UHMWPE irradiated at 25, …
The Wear Behavior Of Cross-Linked Uhmwpe Under Dry And Bovine Calf Serum-Lubricated Conditions
The Wear Behavior Of Cross-Linked Uhmwpe Under Dry And Bovine Calf Serum-Lubricated Conditions
A.S. Md Abdul Haseeb
The present study was performed to investigate the effects of gamma radiation on the wear behavior of unirradiated and irradiated ultra-high-molecular-weight polyethylene (UHMWPE) against Ti-6Al-4V under dry and lubricated conditions at different applied loads. The UHMWPE specimens were exposed directly to nominal doses of 0, 25, 40, 50, and 100 kGy. Scanning electron microscope (SEM) analysis of the worn surface of UHMWPE and Ti-6Al-4V was performed to understand the mechanism of wear involved between the contact surfaces during wear testing. From the wear test results, there were significant differences between the wear of unirradiated UHMWPE and UHMWPE irradiated at 25, …