A Hybrid Constitutive Model For Creep, Fatigue, And Creep-Fatigue Damage, Calvin Stewart
A Hybrid Constitutive Model For Creep, Fatigue, And Creep-Fatigue Damage, Calvin Stewart
Electronic Theses and Dissertations
In the combustion zone of industrial- and aero- gas turbines, thermomechanical fatigue (TMF) is the dominant damage mechanism. Thermomechanical fatigue is a coupling of independent creep, fatigue, and oxidation damage mechanisms that interact and accelerate microstructural degradation. A mixture of intergranular cracking due to creep, transgranular cracking due to fatigue, and surface embrittlement due to oxidation is often observed in gas turbine components removed from service. The current maintenance scheme for gas turbines is to remove components from service when any criteria (elongation, stress-rupture, crack length, etc.) exceed the designed maximum allowable. Experimental, theoretical, and numerical analyses are performed to …