Velocity Effects On The Wear, Friction And Tribochemistry Of Aluminum Mmc Sliding Against Phenolic Brake Pad
A.S. Md Abdul Haseeb
Two aluminum metal matrix composites (MMC) reinforced with 13 vol.% of SiC or B4C particles were made by stir casting followed by hot extrusion. Effects of sliding velocity on the wear, friction and tribochemistry of the worn surfaces of both composites sliding against a commercial phenolic brake pad have been investigated under dry condition. The wear tests were carried out using a pin-on-disc type apparatus at two linear sliding speeds: 1.62 and 4.17 m s-1 under a constant contact pressure of 0.75 MPa for a sliding distance of 5832 m. The coefficient of friction was recorded and wear rate of …
Velocity Effects On The Wear, Friction And Tribochemistry Of Aluminum Mmc Sliding Against Phenolic Brake Pad
A.S. Md Abdul Haseeb
Two aluminum metal matrix composites (MMC) reinforced with 13 vol.% of SiC or B4C particles were made by stir casting followed by hot extrusion. Effects of sliding velocity on the wear, friction and tribochemistry of the worn surfaces of both composites sliding against a commercial phenolic brake pad have been investigated under dry condition. The wear tests were carried out using a pin-on-disc type apparatus at two linear sliding speeds: 1.62 and 4.17 m s-1 under a constant contact pressure of 0.75 MPa for a sliding distance of 5832 m. The coefficient of friction was recorded and wear rate of …
Microstructure And Interface Characteristics Of B4c, Sic And Al2o3 Reinforced Al Matrix Composites: A Comparative Study
A.S. Md Abdul Haseeb
Three aluminium metal matrix composites containing reinforcing particles of B4C, SiC and Al2O3 (0-20vol.%) were processed. The stir-casting manufacturing route followed by hot extrusion was utilized, being one of the cost-effective industrial methods. A clear interfacial reaction product/layer was found at Al-SiC interface for composites held for a relatively long processing time (>30 min). No reaction product was observed at Al-B4C and Al-Al2O3 interfaces at the resolution limit of the SEM used. On the other hand, two secondary phases (alumina and another phase containing aluminium, boron and carbon) were found in the aluminum matrix away from the interface in …
Microstructure And Interface Characteristics Of B4c, Sic And Al2o3 Reinforced Al Matrix Composites: A Comparative Study
A.S. Md Abdul Haseeb
Three aluminium metal matrix composites containing reinforcing particles of B4C, SiC and Al2O3 (0-20vol.%) were processed. The stir-casting manufacturing route followed by hot extrusion was utilized, being one of the cost-effective industrial methods. A clear interfacial reaction product/layer was found at Al-SiC interface for composites held for a relatively long processing time (>30 min). No reaction product was observed at Al-B4C and Al-Al2O3 interfaces at the resolution limit of the SEM used. On the other hand, two secondary phases (alumina and another phase containing aluminium, boron and carbon) were found in the aluminum matrix away from the interface in …