Optimization Of Selective Laser Sintering Process For Fabrication Of Zirconium Diboride Parts, Ming-Chuan Leu, Shashwatashish Pattnaik, Greg Hilmas
Optimization Of Selective Laser Sintering Process For Fabrication Of Zirconium Diboride Parts, Ming-Chuan Leu, Shashwatashish Pattnaik, Greg Hilmas
Mechanical and Aerospace Engineering Faculty Research & Creative Works
Selective Laser Sintering (SLS) was investigated to fabricate Zirconium Diboride (ZrB2) parts for ultra-high temperature applications. Experiments were conducted to determine values of SLS process parameters (laser power, scan speed, line spacing, and layer thickness) that can be used to build ZrB2 parts with high integrity and sharp geometrical features. A sacrificial plate with a proper number of layers (determined from experimentation) separated from the main part was built in order to reduce thermal gradients when building the main part. The sacrificial plate was found to assist in eliminating cracks in the bottom of the main part. …
Freeform Fabrication Of Zirconium Diboride Parts Using Selective Laser Sintering, Ming-Chuan Leu, Erik B. Adamek, Tieshu Huang, Greg Hilmas, Fatih Dogan
Freeform Fabrication Of Zirconium Diboride Parts Using Selective Laser Sintering, Ming-Chuan Leu, Erik B. Adamek, Tieshu Huang, Greg Hilmas, Fatih Dogan
Mechanical and Aerospace Engineering Faculty Research & Creative Works
Using the Selective Laser Sintering (SLS) process, both flexural test bars and 3D fuel injector components have been fabricated with zirconium diboride (ZrB2) powder. Stearic acid was selected as the binder. Values of SLS process parameters were chosen such that the green parts could be built with sharp geometrical features and that the sintered parts could have good mechanical properties. After binder burnout and sintering, the SLS fabricated ZrB2 test bars achieved 80% theoretical density, and the average flexural strength of the sintered samples was 195 MPa. These values demonstrate the feasibility of the SLS process for …