Photoluminescence Spectroscopy Of 4h- And 6h-Sic, William A. Davis
Photoluminescence Spectroscopy Of 4h- And 6h-Sic, William A. Davis
Theses and Dissertations
Typical undoped bulk grown SiC shows n- or p-type conductivity due to residual impurities such as nitrogen, boron, or aluminum. In order to produce high resistivity material, vanadium can be used as a compensating dopant. Since vanadium is an amphoteric dopant in SiC, it produces either a donor state, VSi4+(3d1) → VSi5+(3d0), or an acceptor state, VSi4+(3d1) → VSi3+(3d2). Thus, vanadium doping can compensate both n- and p-type conductivity. In this work, vanadium doped and undoped 4H- and 6H-SiC grown …
The Excitation Mechanism Of Praseodymium-Doped Semiconductors, Paul L. Thee
The Excitation Mechanism Of Praseodymium-Doped Semiconductors, Paul L. Thee
Theses and Dissertations
This study on praseodymium Pr luminescence in AlxGa1-xAs was conducted to enhance the understanding of the excitation mechanism. Pr was implanted at 390 keV with doses from 5 x 1012 to 5 x 1013 sq cm into AlxGa1-xAs x0.0 to 0.50 wafers which were annealed using the rapid thermal annealing RTA method. Low temperature photoluminescence PL was conducted using an Ar-ion laser and Ge detector. PL emissions of Pr from all hosts include peaks near 1.3 and 1.6 µm which are assigned to the intra-4f transitions of 1G4 yielding 3H5 …