Joining Of Copper And Stainless Steel 304l Using Direct Metal Deposition, Xinchang Zhang, Yitao Chen, Tan Pan, Wenyuan Cui, Lan Li, Frank W. Liou

Mechanical and Aerospace Engineering Faculty Research & Creative Works

In the current study, the feasibility of joining pure copper (Cu) and stainless steel 304L (SS304L) through direct metal deposition process was investigated by material characterization. Samples were analyzed in terms of microstructure, elemental distribution, and tensile testing. Direct depositing pure copper on SS304L shows copper was mechanically rather than metallurgical bonded with SS304L due to the poor dissolubility of iron in copper. Iron was diffused into copper with a diluted distance of 1.5 mm and above that, pure copper deposits were obtained. Columnar structure was observed at the copper region near the interface while the columnar grains became finer …