The Effectiveness Of Damage Arrestment Devices In Delaying Fastener-Hole Interaction Failures In Carbon Fiber Polyurethane Foam Composite Sandwich Panels Subjected To Static And Dynamic Loading Under Increased Temperatures, Dominic E. Surano

Master's Theses

A study was conducted to investigate simple, cost-effective manufacturing techniques to delay skin-core delamination, micro-buckling and bearing stress failures resulting from fastener-hole interactions. Composite sandwich panels, with and without damage arrestment devices (DADs), were subjected to monotonic compression at a rate of 5mm per second, and compression-compression fatigue at 50% yield at an amplitude of 65%, under temperatures of 75, 100, 125, 150, 175, and 200 °F.

The sandwiches tested were composed of two-layer cross-weave carbon fiber facesheets, a polyurethane foam core, and an epoxy film adhesive to join the two materials. The most successful method to delay the aforementioned …

An Investigation Of Damage Arrestment Devices Application With Fastener/Hole Interaction, Richard Vincent S. Balatbat

Master's Theses

This thesis presents a parametric study on the effects of how damage arrestment devices application interacts with a fastener in a composite sandwich panel. The primary objective of the damage arrestment device was to prevent the failure of the composite face sheet, such as crack propagation, around the hole/fastener joint. The damage arrestment devices are made of composite strips that are inserted under the face sheet to increase the overall structural strength of the panel and to prevent the propagation of failure along the hole. This was supposed to be a quicker and stronger alternative to potted inserts for composite …