Creep Of Hi-Nicalon™ S Ceramic Fiber Tows At 800°C In Air And In Silicic Acid-Saturated Steam, Scott J. Robertson
Creep Of Hi-Nicalon™ S Ceramic Fiber Tows At 800°C In Air And In Silicic Acid-Saturated Steam, Scott J. Robertson
Theses and Dissertations
A facility was demonstrated that successfully resolved problems highlighted by previous attempts to study SiC fibers in steam. Monotonic tension and creep tests were conducted to characterize the fibers. The tensile strength of the fibers showed little dependence on applied stress rate, indicating a resistance to environmentally assisted crack growth. Climb-controlled diffusion in air and grain boundary sliding in silicic acid-saturated steam were the dominant damage mechanisms. Silicic acid-saturated steam had a degrading effect on the mechanical performance of the fibers, but much less than unsaturated steam environments. The Monkman-Grant relationship was demonstrated for Hi-NicalonTM S fibers and may be …
Tension-Compression Fatigue Of An Oxide/Oxide Ceramic Matrix Composite At Elevated Temperature In Air And Steam Environments, Richard L. Lanser
Tension-Compression Fatigue Of An Oxide/Oxide Ceramic Matrix Composite At Elevated Temperature In Air And Steam Environments, Richard L. Lanser
Theses and Dissertations
Tension-compression fatigue behavior of an oxide-oxide ceramic matrix composite was investigated at 1200°C in air and steam. The composite is comprised of an alumina matrix reinforced with Nextel 720 fibers woven in an eight harness satin weave. The composite relies on a porous matrix for damage tolerance. Compression and tension tests to failure were conducted to characterize basic mechanical properties. Tension-compression fatigue tests were performed at 1 Hz frequency with a ratio of minimum to maximum stress of -1. Maximum stresses ranged from 60-120 MPa. Fatigue run-out (defined as 105 cycles) was achieved in air at 80 MPa and in …
Effect Of Prior Exposure At Elevated Temperatures On Tensile Properties And Stress-Strain Behavior Of Three Oxide/Oxide Ceramic Matrix Composites, Christopher J. Hull
Effect Of Prior Exposure At Elevated Temperatures On Tensile Properties And Stress-Strain Behavior Of Three Oxide/Oxide Ceramic Matrix Composites, Christopher J. Hull
Theses and Dissertations
Thermal stability of three oxide-oxide ceramic matrix composites was studied. The materials studied were NextelTM610/aluminosilicate (N610/AS), NextelTM720/aluminosilicate (N720/AS), and NextelTM720/Alumina (N720/A), commercially available oxide-oxide ceramic composites (COI Ceramics, San Diego, CA). The N610/AS composite consists of a porous aluminosilicate matrix reinforced with laminated woven alumina N610 fibers. The N720/AS and N720/A composites consist of a porous oxide matrix reinforced with laminated, woven mullite/alumina (NextelTM720) fibers. The matrix materials are aluminosilicate in N720/AS and alumina in N720/A. All three composites have no interface between the fibers and matrix, and rely on the porous …